In order to improve the hardness and wear resistance of WC_Ni cemented carbide, a WC_9Ni_1Cr fine-grained cemented carbide was prepared. Using WC powder, Ni powder, Cr powder, W powder and C powder as raw materials, the addition of Cr element can improve the mechanical and magnetic properties of cemented carbide. The mechanism is that Cr element can inhibit the abnormal growth of grains during sintering, and make the internal structure of cemented carbide more uniform and denser. The hardness, densification degree and flexural strength of WC_9Ni_1Cr fine-grained cemented carbide have been greatly improved. The invention can provide a new production process for preparing high-performance WC Ni fine-grained cemented carbide.
【技术实现步骤摘要】
一种WC-9Ni-1Cr细晶硬质合金所属
本专利技术涉及一种硬质合金材料，尤其涉及一种WC-9Ni-1Cr细晶硬质合金。
技术介绍
传统意义上的硬质合金是指将具有优异物理性能的硬质相WC颗粒嵌入低熔点的粘结相Co中，通过粉末冶金方法制备所得到的合金材料。Ni作为一种新型的粘结剂应用到硬质合金时，需在合金中添加耐蚀元素如Cr、Mo等，以进一步强化粘结相，提高合金的耐磨蚀、抗氧化等性能。WC-Ni系无磁硬质合金耐蚀性好，主要原因来自Ni的耐蚀性。通常无磁硬质合金还添加对表面有钝化作用的耐蚀元素Cr，起到固溶强化粘结相、消除磁性、提高抗氧化等作用。细晶硬质合金是碳化物平均晶粒度在0.6~1.00m范围内的硬质合金。铬用于制不锈钢，汽车零件，工具，磁带和录像带等。铬镀在金属上可以防锈，也叫可多米，坚固美观。铬可用于制不锈钢。红、绿宝石的色彩也来自于铬。作为现代科技中最重要的金属，以不同百分比熔合的铬镍钢千变万化，种类繁多，令人难以置信。
技术实现思路
本专利技术的目的是为了改善WC-Ni硬质合金的硬度、耐磨性，设计了一种WC-9Ni-1Cr细晶硬质合金。本专利技术解决其技术问...
【技术保护点】
1.一种WC‑9Ni‑1Cr细晶硬质合金的制备原料包括：主要原料为总碳含量6.15%、游离碳含量0.032%、氧含量0.06%、费氏粒度1.15μm的WC粉和纯度≥99.9%、费氏粒度2.60μm的Ni粉，辅料为纯度为99.95%、费氏粒度为48μm的Cr，纯度为99.95%、费氏粒度1.10μm的W和含碳量≥99.5%C粉。
【技术特征摘要】
1.一种WC-9Ni-1Cr细晶硬质合金的制备原料包括：主要原料为总碳含量6.15%、游离碳含量0.032%、氧含量0.06%、费氏粒度1.15μm的WC粉和纯度≥99.9%、费氏粒度2.60μm的Ni粉，辅料为纯度为99.95%、费氏粒度为48μm的Cr，纯度为99.95%、费氏粒度1.10μm的W和含碳量≥99.5%C粉。2.根据权利要求1所述的WC-9Ni-1Cr细晶硬质合金，其特征是WC-9Ni-1Cr细晶硬质合金的制备步骤为：将原料及辅料粉末按照实验设计方案进行准确称量、配料，将其加至到2.4L球磨筒中进行球磨，球磨时间为36h，球磨机转速为72r/min，球磨后，将料浆在真空干燥柜中进行搞糟，干燥温度为65℃，干燥时间为100min，然后过50目筛网得到WC-9Ni-1Cr混合粉末，将制好的混合粉末加至单柱校正压装液压机中进行压制成形，压制压力为80MPa，保压时间为10s，随后将压坯在氢气脱蜡低压烧结一体炉中进行低压烧结，最高烧结温度为1470℃，保温90min，烧结压力为5Mpa。3.根据权利要求1所述的WC-9Ni-1...