In order to improve the hardness and wear resistance of WC_Ni cemented carbide, a high performance non-magnetic WC_15Ni cemented carbide was developed. Using WC powder, electrolytic Ni powder, Cr3C2 powder and carbon black as raw materials, the mechanical properties of cemented carbide can be improved by adding carbon elements. Its mechanism is that it can restrain the growth of cemented carbide grain during sintering process, and make the cemented carbide have uniform phase composition and fewer defects. When the content of carbon element is 7%, the microstructures have no defects and excellent properties. The average transverse fracture strength reaches 3300 MPa. The hardness, densification degree and bending strength of WC_15Ni high performance non-magnetic cemented carbide have been greatly improved. The invention can provide a new production process for preparing high performance WC Ni cemented carbide.
【技术实现步骤摘要】
一种WC-15Ni高性能无磁硬质合金所属
本专利技术涉及一种硬质合金材料，尤其涉及一种WC-15Ni高性能无磁硬质合金。
技术介绍
硬质合金是一种具有高硬度、高强度、高韧性的工具材料，在切削刀具和轴承等摩擦磨损较严重的场合应用较多。传统意义上的硬质合金是指将具有优异物理性能的硬质相WC颗粒嵌入低熔点的粘结相Co中，通过粉末冶金方法制备所得到的合金材料。然而，随着现代工业的发展，硬质合金的应用范围正在不断扩大，除了对硬度和强度之外，对硬质合金的耐腐蚀性能也有了较高的要求。常见WC-Co系硬质合金中粘结相Co易受化学介质侵蚀，使碳化物组成的硬质相骨架结构脆弱，在磨擦作用下硬质相晶粒剥落，加剧磨蚀、磨损。WC-Ni系无磁硬质合金耐蚀性好，主要原因来自Ni的耐蚀性。无磁合金，是指没有磁性或者弱磁性的硬质合金材料。由于生产磁性材料的成型模具要求采用无磁性的材料，以往一直用无磁钢，其模具性能较差，硬度低，使用寿命短，而且使用一段时间过后模具内壁严重拉毛、变形等，进而影响磁性材料的尺寸精度和表面质量。而今采用无磁硬质合金，以其优异的性能代替无磁钢可以成倍的提高工作效率。专利技术...
【技术保护点】
1.一种WC‑15Ni高性能无磁硬质合金的制备原料包括：平均粒度为0.6μm的WC粉、电解Ni粉、Cr3C2粉、碳黑。
【技术特征摘要】
1.一种WC-15Ni高性能无磁硬质合金的制备原料包括：平均粒度为0.6μm的WC粉、电解Ni粉、Cr3C2粉、碳黑。2.根据权利要求1所述的WC-15Ni高性能无磁硬质合金，其特征是WC-15Ni高性能无磁硬质合金的制备步骤为：将原料粉末按实验设计方案进行称量、配料，然后与成形剂石蜡、球磨介质无水酒精一起加入到50L球磨罐中，球料比为1:3，球磨时间为48H，将球磨后的粒料进行干燥、过筛，然后造粒后制得混合料，混合料经模压成形、冷等静压密度均匀化、真空烧结、热等静压处理、机加工，制备出测试试样和密封环成品，真空烧结温度1400℃，保温时间1H；热等静压处理温度1400℃，压力150MPa，保温时间2H。3.根据权利要求1所述的WC-15Ni高性能无磁硬质合金，其特征是WC-15Ni...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。