The present invention provides a depolarizing spectroscopic prism and a preparation method thereof, in which the depolarizing spectroscopic prism comprises at least two prism substrates, and a depolarizing spectroscopic film is plated between the two prism substrates. The depolarizing spectroscopic film comprises a metal layer having absorption characteristics and a dielectric layer plated outside the metal layer, and a bonding strengthening layer is plated between the dielectric layer and the prism substrates. The invention solves the problem that the existing spectroscopic prism can not place the spectroscopic film for a long time due to the poor adhesion and hardness of the film layer, further improves the preparation quality of the process and reduces the production cost.
【技术实现步骤摘要】
一种消偏分光棱镜及其制备方法
本专利技术涉及光学镀膜
，具体涉及一种消偏分光棱镜及其制备方法。
技术介绍
消偏分光棱镜是指一个立方体棱镜，它在指定的使用波段范围内，对不同偏振态的入射光具有接近相同的分光特性，即对入射光的偏振态不敏感的分光棱镜。这种元件在干涉仪、医疗仪器和经纬仪等领域有广泛的应用。如图1和图2所示，消偏分光棱镜由两个半立方体组成，其中，在一个半立方体1a的斜面镀有消偏分光膜9a，然后，用与玻璃基底折射率接近相等的透明胶水将两个半立方体1a胶合在一起，用紫外线进行固化后，得到一个完整的消偏分光棱镜。在图1和图2的基础上，当涉及到宽波段消偏时，需要用金属银或硅等具有吸收特性的材料作为消偏材料，消偏分光膜用到的材料有ZnS、Al2O3、Ag、Si、TiO2、SiO2等材料。对消偏要求较高时，即要求不同偏振态的分光特性差异要求很小的时候，就得选择金属银作为膜料，并相应选择ZnS、Al2O3作为介质匹配膜料。进一步地，在用电子束蒸发进行真空镀膜时，由于有金属银参与镀膜，银在高温下很容易氧化。为防止银的氧化，半立方体棱镜在镀膜时要处于常温状态，不能加温，...
【技术保护点】
1.一种消偏分光棱镜，其特征在于，包括至少两块棱镜基底，两块所述棱镜基底之间镀有消偏分光膜，所述消偏分光膜包括具有吸收特性的金属层以及镀于所述金属层表面的介质层，所述介质层与所述棱镜基底之间镀有粘结加强层。
【技术特征摘要】
1.一种消偏分光棱镜，其特征在于，包括至少两块棱镜基底，两块所述棱镜基底之间镀有消偏分光膜，所述消偏分光膜包括具有吸收特性的金属层以及镀于所述金属层表面的介质层，所述介质层与所述棱镜基底之间镀有粘结加强层。2.根据权利要求1所述的消偏分光棱镜，其特征在于，所述粘结加强层包括打底层以及过渡层，所述过渡层镀于所述介质层的表面，所述打底层镀于所述过渡层的表面以供与所述棱镜基底粘合。3.根据权利要求2所述的消偏分光棱镜，其特征在于，所述打底层为SiO2膜层，所述过渡层为Al2O3膜层。4.根据权利要求1至3任一所述的消偏分光棱镜，其特征在于，所述有粘结加强层的表面还镀有防水保护层。5.根据权利要求4所述的消偏分光棱镜，其特征在于，所述防水保护层为SiO2膜层。6.根据权利要求1所述的消偏分光棱镜，其特征在于，每块所述棱镜基底为三角棱镜或直角棱镜，所述消偏分...
【专利技术属性】
技术研发人员：汤兆胜，罗新华，
申请(专利权)人：江西兆九光电技术有限公司，
类型：发明
国别省市：江西,36