The invention relates to the field of geological adsorption technology, and provides a travertine brick, which is prepared from raw materials including 70-90% travertine base material, 9-29.9% calcium-based adhesives, 0.1-1% travertine reinforcing agent, a mixture of calcium oxide, calcium hydroxide and calcium bicarbonate, and a travertine reinforcing agent, which is wood debris and the wood debris is fine. Long fibrous. The travertine brick provided by the invention has good compatibility with travertine landscape geology, can ensure that the color, density and permeability coefficient of travertine brick are consistent with travertine, can not cause permanent damage to travertine geology, and can realize in-situ restoration of travertine geology. The travertine brick obtained by the invention has high compressive strength and good water resistance.
【技术实现步骤摘要】
一种钙华砖及其制备方法和应用
本专利技术涉及地质吸附
，特别涉及一种钙华砖及其制备方法和应用。
技术介绍
钙华是富含碳酸氢根的地表水，在适当的物理、化学或生物条件下，接近和/或露出于地表时，因二氧化碳大量逸出而形成的碳酸钙化学沉淀物。这些沉淀物随水流的游移和水循环系统的变化而变迁，形成钙华景观。我国四川省“世界自然遗产”九寨沟自然风景区不仅拥有着巨大的旅游景观价值，同时景区内钙华也可以作为高分辨率古气候环境重建的重要载体，而越来越受到人们关注。因为人和自然原因，钙华景观在不同程度上受到了退化和破坏。例如：九寨沟自然风景区于2017年8月8日21时19分，发生Ms7.0地震。此次地震造成九寨沟火花海、诺日朗等景点受损情况十分严重。火花海钙华坝体溃坝长度约20米，占坝体长度的5％；这次地震造成诺日朗瀑布局部发生垮塌，钙华坝体溃坝长度约20m，约占瀑布整体宽度的6.25％，垮塌段后侧发育裂长4～5m、宽约0.5m，出现多处裂缝、暗流，造成水量严重减少。受损钙华景观的修复，需要重点考虑到钙华原有的地质特点，但是常规水利工程岸坡的维护或修补用材料如钢筋混凝土与钙华地质...
【技术保护点】
1.一种钙华砖，由包括以下质量百分含量的原料制备得到：钙华基料 70～90％；钙基胶黏剂 9～29.9％；钙华增强剂 0.1～1％；所述钙基胶黏剂为氧化钙、氢氧化钙和碳酸氢钙的混合物；所述钙华增强剂为木质碎屑，所述木质碎屑为细长纤维状。
【技术特征摘要】
1.一种钙华砖，由包括以下质量百分含量的原料制备得到：钙华基料70～90％；钙基胶黏剂9～29.9％；钙华增强剂0.1～1％；所述钙基胶黏剂为氧化钙、氢氧化钙和碳酸氢钙的混合物；所述钙华增强剂为木质碎屑，所述木质碎屑为细长纤维状。2.根据权利要求1所述的钙华砖，其特征在于，所述钙华基料为废弃钙华，所述钙华基料的粒径为75～2000μm。3.根据权利要求1所述的钙华砖，其特征在于，所述氧化钙、氢氧化钙和碳酸氢钙的质量比为2～8：8～12：1～10。4.根据权利要求1所述的钙华砖，其特征在于，所述木质碎屑为麻纤维或松针。5.根据权利要求1或4所述的钙华砖，其特征在于，所述木...
【专利技术属性】
技术研发人员：代群威，闵世杰，党政，邓远明，董发勤，
申请(专利权)人：西南科技大学，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。