The invention discloses a nano-breaking material and its application in the treatment of aging solution before plating. The raw materials of the nano-breaking material are as follows: zeolite 35%-45%, fly ash 20%-35%, diatomite 8%-16%, clay 5%-15%, bentonite 25%-45%, binder 5%-8% by weight percentage. The present invention first uses nano-breaking material to pretreat the aging solution of electroplating pretreatment. The purpose of pretreatment is to decompose the strong complex compounds in the waste liquid and free the heavy metals. Then, the heavy metals in the waste liquid can be thoroughly removed by chemical chelating capture and coagulation precipitation, so that the heavy metals in the waste liquid can be treated within the GB21900 2008 Table 2 standard and meet the requirements.
【技术实现步骤摘要】
一种纳米破络材料及其在电镀前处理老化液处理中的应用
本专利技术属于废水处理
，具体涉及一种纳米破络材料及其在电镀前处理老化液处理中的应用。
技术介绍
电镀、化学镀、转化膜处理等表面处理工艺的共同特点，都是在被镀材料基体表面发生化学或电化学反应，所以基本表面质量的好坏直接影响到镀层质量的好坏。电镀前处理就是对基体表面的油污、锈膜、氧化皮以及各种润滑剂、脱膜剂进行清洁，使基体表面符合电镀要求的工艺总称。它一般包含基本表面机械研磨、抛光，化学除油，电化学除油，有机溶剂除油，酸洗等工序。电镀前处理工作液在工作时，基本表面污染物会溶入溶液中，随着工作时间的推进，其溶液中的污染物(杂质)会累积，当累积到一定程度后，就会影响到基体表面的处理。此时，其工作液就要进行更换，这部分报废的工作液就是电镀前处理老化液。由于它成份复杂，污染物深度高，所以非常难以处理。
技术实现思路
本专利技术的目的是针对上述现有技术的不足，提供一种纳米破络材料，并将其应用在电镀前处理老化液处理中，通过采用纳米破络材料对电镀前处理老化液进行预处理，使重金属游离，然后再经化学螯合捕捉、混凝沉淀予以彻底去除。...
【技术保护点】
1.一种纳米破络材料，其特征在于：原料以重量百分比计包括：沸石35％‑45％，粉煤灰20％‑35％，硅藻土8％‑16％，白土5％‑15％，膨润土25％‑45％，粘结剂5％‑8％，所有原料的重量百分比之和为100％。
【技术特征摘要】
1.一种纳米破络材料，其特征在于：原料以重量百分比计包括：沸石35％-45％，粉煤灰20％-35％，硅藻土8％-16％，白土5％-15％，膨润土25％-45％，粘结剂5％-8％，所有原料的重量百分比之和为100％。2.权利要求1所述的纳米破络材料在电镀前处理老化液处理中的应用。3.根据权利要求2所述的应用，其特征在于：包括以下步骤：步骤1，将收集好的电镀前处理老化液与纳米破络材料混合，调节pH值为2.5-3.0，进行预处理；步骤2，将预处理液导入化学混凝反应系统，调节预处理液pH值至10.5以上，依次经过重捕反应、混凝反应和絮凝反应后，进行沉淀、中和即可达标排放。4.根据权利要求3所述的应用，其特征在于：步骤1中采用硫酸溶液调节pH值，预处理的时间为2小时。5.根据权利要求3所述的应用，其特征在...
【专利技术属性】
技术研发人员：黄辉樟，
申请(专利权)人：厦门科霖达环保科技有限公司，
类型：发明
国别省市：福建,35
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。