The invention discloses a preparation method of electroplating heavy metal chelating agent, which mixes inorganic chelates in the first stirring device, organic chelates in the second stirring device, and then mixes the two kinds of mixtures again. The electroplating heavy metal chelating agent is obtained by dripping weak salts and organic amines and stirring and stationary. The invention provides a preparation method of electroplating heavy metal chelating agent, which has simple preparation method and short reaction time. The electroplating heavy metal chelating agent obtained by the invention has a wide range of raw materials, low price, stable performance, long service life, and can be preserved and used for a long time.
【技术实现步骤摘要】
一种电镀重金属螯合剂的配制方法
本专利技术涉及一种螯合剂的制备方法，特别是一种电镀重金属螯合剂的配制方法。
技术介绍
重金属螯合剂，通常也被叫做重金属离子析出剂、重金属捕集剂等，是一种与重金属离子强力螯合的化工药剂，广泛应用在电镀业，电子工业，有色、钢铁冶炼业，照相实验室和胶片洗印厂。能在常温和很宽的pH值条件范围内，与废水中的多种重金属离子进行化学反应，并在短时间内迅速生成不溶性、低含水量、容易过滤去除的絮状沉淀，从而达到从水中去除重金属离子的化学品被称为重金属螯合剂。现有的传统重金属处理技术存在工艺相对复杂、耗能高、易产生二次污染等问题。特别是在处理低含量重金属污染废水使其操作费用和原材料成本相对过高。
技术实现思路
本专利技术的目的是为了解决上述现有技术的不足而提供一种成本较低、效果显著且环保的电镀重金属螯合剂的配制方法。为了实现上述目的，本专利技术所设计的一种电镀重金属螯合剂的配制方法，包括以下步骤：步骤一、在第一搅拌装置中加入水，按重量份将40-50份纳米氧化铝、10-15份硫化钠、5-15份纳米氧化钛、5-20份EDTA依次加入第一搅拌装置中，调节温度为8...
【技术保护点】
1.一种电镀重金属螯合剂的配制方法，其特征在于：包括以下步骤：步骤一、在第一搅拌装置中加入水，按重量份将40‑50份纳米氧化铝、10‑15份硫化钠、5‑15份纳米氧化钛、5‑20份EDTA依次加入第一搅拌装置中，调节温度为80‑100℃；步骤二、在第二搅拌装置加入丙酮或乙醇溶液，在按重量份将20‑30份羧甲基纤维素、0.5‑1份聚羧酸、5‑10份三巯三嗪三钠和5‑10份葡萄糖依次加入第二搅拌装置中，调节温度为60‑80℃；步骤三、将第一搅拌装置和第二搅拌装置的混合物进行搅拌，然后缓慢滴加弱酸盐，控制pH值为7‑10.5，滴加时间0.5‑2小时，稳定搅拌1‑3小时，缓慢滴加有...
【技术特征摘要】
1.一种电镀重金属螯合剂的配制方法，其特征在于：包括以下步骤：步骤一、在第一搅拌装置中加入水，按重量份将40-50份纳米氧化铝、10-15份硫化钠、5-15份纳米氧化钛、5-20份EDTA依次加入第一搅拌装置中，调节温度为80-100℃；步骤二、在第二搅拌装置加入丙酮或乙醇溶液，在按重量份将20-30份羧甲基纤维素、0.5-1份聚羧酸、5-10份三巯三嗪三钠和5-10份葡萄糖依次加入第二搅拌装置中，调节温度为60-80℃；步骤三、将第一搅拌装置和第二搅拌装置的混合物进行搅拌，然后缓慢滴加弱酸盐，控制pH值为7-10.5，滴加...
【专利技术属性】
技术研发人员：胥小红，
申请(专利权)人：宁波君笙环保科技有限公司，
类型：发明