The present invention relates to a method for preparing boron-doped carbon nitride and its products and applications. The method for hydrothermal reaction of melamine with boric acid promotes chemical reaction of boron atom with melamine to form atom-level mixing of boron and carbon and nitrogen elements. On the other hand, hydrothermal treatment of melamine in acidic environment can form a supramolecular structure. Carbon nitride lamellar structure can be separated in subsequent calcination process, and then the precursor synthesized by reaction can be calcined to prepare boron-doped carbon nitride with uniform doping and thinner lamellar structure. The boron doped carbon nitride prepared by the method of the invention has uniform element doping, thinner layer, better photocatalytic performance, simple preparation operation and low difficulty, and is suitable for magnifying production.
【技术实现步骤摘要】
硼掺杂氮化碳的制备方法及其产品和应用
本专利技术属于纳米材料制备领域，具体涉及一种硼掺杂氮化碳的制备方法及其产品和应用。
技术介绍
能源危机和环境污染是人类社会可持续发展中所面临的两个重大战略问题。随着传统化石能源如煤、石油、天然气等的日益枯竭以及在使用过程中带来的一系列环境问题，对于清洁能源的有效利用，水、空气的净化和控制领域的问题显得迫切而重要。光催化过程能将太阳能转变为化学能，通过光催化氧化还原反应以实现水的分解，降解、矿化环境毒素，具有稳定、高效、无污染等优点。因此，以光催化材料为核心的光催化技术对处在经济社会转型关键时期的我国具有极为重要的意义。聚合物半导体氮化碳作为一种新型的非金属可见光光催化剂，具有独特的电子结构、可见光催化活性、化学与热稳定性好、无毒且制备简易、不含金属等特点，但氮化碳的光致电子-空穴对复合率较高，导致其催化活性受到限制，故通过适当的方式对光催化剂进行修饰改性来提高光催化活性，开发可见光响应、高效和稳定的光催化材料。为了改善这一缺点，现在通常利用掺杂的方法改善其电子结构和表面性质。掺杂后电子结构发生了改变，掺杂元素与氮化碳原有的分子...
【技术保护点】
1.一种硼掺杂氮化碳的制备方法，其特征在于将三聚氰胺与硼酸进行水热反应，然后，将反应合成的前驱体进行焙烧，制备得到均匀掺杂，且片层结构更薄的硼掺杂氮化碳，包括如下步骤：1）三聚氰胺/硼酸/水按质量比1:（0.01～1）:（5～100）称取，首先将三聚氰胺与硼酸以及水加入水热反应釜中，搅拌均匀之后放入烘箱中进行水热反应，然后将产物过滤洗涤真空干燥即得前驱体；2）将在上述得到的前驱体研磨粉碎之后放入坩埚中，在马弗炉中以2.5℃/分钟的升温速率升温到400～600℃，保温1～5小时，得到的粉末即为硼掺杂氮化碳。
【技术特征摘要】
1.一种硼掺杂氮化碳的制备方法，其特征在于将三聚氰胺与硼酸进行水热反应，然后，将反应合成的前驱体进行焙烧，制备得到均匀掺杂，且片层结构更薄的硼掺杂氮化碳，包括如下步骤：1）三聚氰胺/硼酸/水按质量比1:（0.01～1）:（5～100）称取，首先将三聚氰胺与硼酸以及水加入水热反应釜中，搅拌均匀之后放入烘箱中进行水热反应，然后将产物过滤洗涤真空干燥即得前驱体；2）将在上述得到的前驱体研...
【专利技术属性】
技术研发人员：何丹农，徐少洪，王敬锋，林琳，陈振，金彩虹，
申请(专利权)人：上海纳米技术及应用国家工程研究中心有限公司，
类型：发明
国别省市：上海,31