A preparation method of solid spherical tin electrode material for sodium ion battery anode growth on carbon cloth is described. 1) Carbon cloth is pretreated. Carbon cloth is first cut and treated by anodic oxidation in hydrothermal electrophoresis for 2 5 minutes, which increases active functional groups on the surface of carbon cloth and makes it easier to adhere to metal ions; 2) Polyvinylpyrrolidone is dissolved in a mixture of ethanol and glycerol to obtain solution A1. SnCl 2.2H 2 was added to solution A1, and then the solution A2 and Sn in solution A2 were obtained by ultrasonic treatment.
【技术实现步骤摘要】
一种钠离子电池负极用在碳布上生长实心球状锡电极材料的制备方法
本专利技术属于钠离子电池负极柔性电极
，特别涉及一种钠离子电池负极用在碳布上生长实心球状锡电极材料的制备方法。
技术介绍
目前，钠离子电池负极主要采用碳石墨化负极材料，但是碳基负极材料的储钠容量不高，并且制备条件复杂。因此，开发新型的具有高容量和高倍率且制备方法简单的负极材料很有意义。在对负极材料的研究中，发现如Sn、Si、Al、Sb等可与钠形成合金的金属或合金材料具有远远大于石墨的理论容量，引起了电池材料界的广泛关注。然而，合金类材料具有很大的体积效应，导致在充放电过程中材料的粉化脱落，降低了电池的效率和循环性能，极大地影响了这类材料的实际应用。而将负极材料纳米化、与碳基材料复合以及控制微观结构等技术被报道能够一定程度的缓解体积膨胀带来的问题。LiuZhiming等人以部分还原的SnO2纳米粒子(SnO2/Sn@C)，采用静电纺丝法制备了一维(1-D)碳纳米纤维，并采用了碳涂层和热还原工艺。部分还原的Sn与碳纤维结合，提供了比SnO2更好的嵌钠/脱钠机制。SnO2/Sn@C电极做钠离子电池负极材...
【技术保护点】
1.一种钠离子电池负极用在碳布上生长实心球状锡电极材料的制备方法，其特征在于，包括以下步骤；1)对碳布进行预处理，先将碳布裁剪成(1.5～5)×(1.5～5cm)的尺寸，在水热电泳仪中阳极氧化处理碳布2‑5min，使碳布表面增加活性官能团，更易附着生长金属离子；2)将0.94～1.91g的聚乙烯吡咯烷酮(PVP)溶于5‑20mL乙醇和5‑20mL甘油混合液中得溶液A1，向溶液A1中加入0.47～1.91g的SnCl2·2H2O，然后超声处理(使聚乙烯吡咯烷酮分子与Sn2+充分作用)得溶液A2，溶液A2中Sn2+的浓度为0.01‑0.21mol·L‑1，向溶液A2中加入处理好...
【技术特征摘要】
1.一种钠离子电池负极用在碳布上生长实心球状锡电极材料的制备方法，其特征在于，包括以下步骤；1)对碳布进行预处理，先将碳布裁剪成(1.5～5)×(1.5～5cm)的尺寸，在水热电泳仪中阳极氧化处理碳布2-5min，使碳布表面增加活性官能团，更易附着生长金属离子；2)将0.94～1.91g的聚乙烯吡咯烷酮(PVP)溶于5-20mL乙醇和5-20mL甘油混合液中得溶液A1，向溶液A1中加入0.47～1.91g的SnCl2·2H2O，然后超声处理(使聚乙烯吡咯烷酮分子与Sn2+充分作用)得溶液A2，溶液A2中Sn2+的浓度为0.01-0.21mol·L-1，向溶液A2中加入处理好的碳布；3)向搅拌后的溶液A2中加入10～20ml水合肼溶液，利用水合肼将碳布上的Sn2+还原为Sn单质，然后将得到的碳布在60℃下真空干燥6～12h得到实心球状锡电极材料。2.根据权利要求1所述的一种钠离子电池负极用在碳布上生长实心球状锡电极材料的制备方法，其特征在于，所述步骤1)碳布为亲水性碳布。3.根据权利要求1所述的一种钠离子电池负极...