The invention discloses an anti-fouling hand-feeling coating, which comprises the following components: 40-70 weight parts of methyl vinyl organosilicon polymer, 3-10 weight parts of spherical organosilicon modified polyurethane elastomer powder, 6-12 weight parts of hydrogen-containing silicone oil, 0.5-3 weight parts of siloxane coupling agent, 0.5-3 weight of inhibitor, 8-25 weight parts of white carbon black, 60-120 weight parts of polyurethane elastomer powder. The preparation method and application of the anti-fouling hand-feeling paint are also provided. Through the combination of the above components, the paint has a delicate and smooth feel, excellent apparent quality, heat resistance, friction resistance and UV aging resistance, as well as good anti-fouling performance.
【技术实现步骤摘要】
一种抗污型手感涂料及其制备方法和应用
本专利技术涉及涂料
，具体涉及一种抗污型手感涂料及其制备方法，所述抗污型手感涂料可用于LSR、TPU、TPE、TPSIV等多种热塑性基材的表面涂装。
技术介绍
液体硅橡胶(LSR)、热塑性聚氨酯弹性体(TPU)、热塑性弹性体(TPE)、热塑性有机硅弹性体(TPSIV)具有优异的耐磨、耐油、透明性和弹性，在日用品、体育用品、玩具、电气、电子、电器、化工、建筑、汽车、仪表、机械装饰材料等领域得到广泛应用。但是这种材料还存在手感生硬、不耐脏、易产生静电等弊端，从而限制了其在某些领域的应用。为克服这一缺陷，市场上出现了PU弹性漆等保护性的涂料，这类产品主要以聚酯、聚氨酯改性的弹性体作为树脂主体，仍然存在易老化、发粘、不抗污等缺点，难以全面满足客户需求，此外，其适用范围窄，大多只能适用于一种材料，如需对不同类型材质进行涂装，则需要分别适用不同的涂料，影响使用便利性。因此，亟待研究出一种新型保护涂料，满足对上述材料的附着力和适用性的同时兼顾手感、耐磨、抗污、防尘、耐老化等综合性能。
技术实现思路
针对现有技术存在的问题，本专利技术提供一...
【技术保护点】
1.一种抗污型手感涂料，其特征在于，包括以下组分：40～70重量份的甲基乙烯基有机硅聚合物、3～10重量份的球状有机硅改性聚氨酯弹性体粉末、6～12重量份的含氢硅油、0.5～3重量份的硅氧烷偶联剂、0.5～3重量份的抑制剂、8～25重量份的白炭黑、60～120重量份的有机溶剂、2～5重量份的过渡金属催化剂。
【技术特征摘要】
1.一种抗污型手感涂料，其特征在于，包括以下组分：40～70重量份的甲基乙烯基有机硅聚合物、3～10重量份的球状有机硅改性聚氨酯弹性体粉末、6～12重量份的含氢硅油、0.5～3重量份的硅氧烷偶联剂、0.5～3重量份的抑制剂、8～25重量份的白炭黑、60～120重量份的有机溶剂、2～5重量份的过渡金属催化剂。2.根据权利要求1所述的抗污型手感涂料，其特征在于，所述甲基乙烯基有机硅聚合物的分子量为15～30万，乙烯基含量为0.2～1.0％。3.根据权利要求1所述的抗污型手感涂料，其特征在于，所述含氢硅油的含氢量为1～2％。4.根据权利要求1所述的抗污型手感涂料，其特征在于，所述过渡金属催化剂为Pt络合物，用量为2500～3000ppm。5.根据权利要求1所述的抗污型手感涂料，其特征在于，所述有机溶剂采用无味煤油、乙酸丁酯、乙酸乙酯和正庚烷复...
【专利技术属性】
技术研发人员：杨庆彪，李平，王卫国，缪培凯，吕国强，杨波，符饶生，凌云剑，伍松，
申请(专利权)人：湖南松井新材料股份有限公司，
类型：发明
国别省市：湖南,43