The invention discloses a graphene composite material and a preparation method thereof. The graphene composite material comprises polyethylene, graphene, zinc stearate, chitosan, octyltrimethylammonium chloride, cocktail powder, sodium citrate, Zanthoxylum powder and triethanolamine dodecyl sulfate. The graphene composite material of the invention can effectively improve the antimicrobial time through the synergistic effect of raw material compounding, and its antimicrobial effect is good. The bactericidal rate of E. coli and Staphylococcus aureus can reach 98.8% and 93.6%, respectively. The preparation process is simple, and is beneficial to industrialized production.
【技术实现步骤摘要】
一种石墨烯复合材料及其制备方法和应用
本专利技术涉及一种石墨烯复合材料及其制备方法和应用，属于新材料领域。
技术介绍
石墨烯是一种由碳原子以sp2杂化轨道组成六角型呈蜂巢晶格的二维碳纳米材料。石墨烯具有优异的光学、电学、力学特性，在材料学、微纳加工、能源、生物医学和药物传递等方面具有重要的应用前景，被认为是一种未来革命性的材料。石墨烯改性技术在石墨烯应用方面已经很常见了，然而，采用协同抗菌剂改性石墨烯的报道很少。目前市售的复合材料大多只致力于研究其抗撕裂等力学性能，对于其抗菌防腐性研究的很少。有些抗菌复合材料将银纳米颗粒负载在塑料上制备而成，然而这种抗菌复合材料不稳定，银纳米颗粒易脱落致使其抗菌性能受影响，不利于长时间使用。研制一种力学性能优异、抗菌效果好的复合材料，是从业者们致力于研究的方向。
技术实现思路
为了解决以上现有技术中存在的复合材料力学性能和抗菌性往往不能兼备的问题，本专利技术提供了一种力学性能和抗菌性均优异的石墨烯复合材料。本申请还提供了所述石墨烯复合材料的制备方法。本专利技术还提供了所述石墨烯复合材料的应用。本专利技术是通过如下措施实现的：一种石墨烯...
【技术保护点】
1.一种石墨烯复合材料，其特征在于，由以下重量份数的原料制成：聚乙烯88‑150份、石墨烯4‑8份、硬脂酸锌6‑10份、壳聚糖2‑6份、辛基三甲基氯化铵1‑7份、凤尾草粉1‑4份、柠檬酸钠2‑6份、花椒粉1‑4份、十二烷基硫酸三乙醇胺4‑7份。
【技术特征摘要】
1.一种石墨烯复合材料，其特征在于，由以下重量份数的原料制成：聚乙烯88-150份、石墨烯4-8份、硬脂酸锌6-10份、壳聚糖2-6份、辛基三甲基氯化铵1-7份、凤尾草粉1-4份、柠檬酸钠2-6份、花椒粉1-4份、十二烷基硫酸三乙醇胺4-7份。2.根据权利要求1所述的石墨烯复合材料，其特征在于，由以下重量份数的原料制成：聚乙烯115-138份、石墨烯5-7份、硬脂酸锌7-9份、壳聚糖3-5份、辛基三甲基氯化铵2-6份、凤尾草粉2-3份、柠檬酸钠3-4份、花椒粉2-3份、十二烷基硫酸三乙醇胺5-6份。3.根据权利要求1所述的石墨烯复合材料，其特征在于，由以下重量份数的原料制成：聚乙烯127份、石墨烯6份、硬脂酸锌8份、壳聚糖4份、辛基三甲基氯化铵5份、凤尾草粉2.6份、柠檬酸钠3.7份、花椒粉2.4份、十二烷基硫酸三乙醇胺5.5份。4.一种根据权利要求1-3中任一所述的石墨烯复合材料的制备方法，其特征在于，包括以下步骤：(1)称取聚乙烯、石墨烯、硬脂酸锌、壳聚糖、辛基三甲基氯化铵、凤尾草粉、柠檬酸钠、花椒粉和十二烷基硫酸三乙醇胺，备用；(2)将石墨烯、硬脂酸锌、辛基三甲基氯化铵和十二烷基硫酸三乙醇胺混合，置于65-78℃下搅拌反应3-5h；(...