A wastewater treatment material based on banana biochar includes biochar, bismuth ferrite and carrier made from banana. The biochar and bismuth ferrite are loaded on the carrier, and the weight ratio of the biochar and bismuth ferrite is 1:30 15:2. The composite material pellet of the invention has the advantages of large growth amount of banana, easy availability of banana leaves and reusable utilization of resources. Bismuth ferrite is easy to prepare. The composite material ball of the invention has simple recovery and separation method after treatment and can be reused. The manufacturing method of the composite material ball of the invention is simple, does not need large-scale mechanical equipment and human and material resources, and can be produced in large quantities.
【技术实现步骤摘要】
一种基于美人蕉生物炭的废水处理材料、制备方法和应用
本专利技术涉及一种废水处理材料，尤其涉及一种处理含有亚甲基蓝的废水的基于美人蕉生物炭的废水处理材料、制备方法和应用。
技术介绍
亚甲基蓝外观为深绿色青铜光泽结晶(三水合物)，可溶于水、乙醇，不溶于醚类。亚甲基蓝在水中呈碱性并且有一定的毒性，广泛应用于化学指示剂、染料、生物染色剂和药物等领域。存在于废水中的亚甲基蓝易造成废水色度偏高，且有研究表明，废水中的染料对环境安全和人体健康影响较大，含量过高的染料废水会引起人体过敏、皮肤发炎、癌症和变异等不良反应。因此，消除印染废水中的有毒物(如亚甲基蓝等)的研究一直受到重视。目前，以亚甲基蓝为研究目标的处理方法大致包括物理化学方法、化学法和生物法等三大类。物化法包括膜分离技术、高级氧化法、吸附法等。其中膜分离技术膜堵塞问题严重，费用高昂Fendon及类Fendon氧化法工艺条件苛刻，运转费用高，产生剩余污泥较多。相对于这类处理方法，吸附法可利用多孔状固体的粉末或颗粒的物理吸附和化学吸附性能，使废水中的污染物吸附于多孔物质表面而被去除，具有费用低、易于设计、设备简单、操作方便...
【技术保护点】
1.一种基于美人蕉生物炭的废水处理材料，其特征在于：包括由美人蕉制作而成的生物炭、铁酸铋和载体，所述的生物炭和铁酸铋负载在载体上；所述生物炭和铁酸铋的重量比为1:30‑15:2。
【技术特征摘要】
1.一种基于美人蕉生物炭的废水处理材料，其特征在于：包括由美人蕉制作而成的生物炭、铁酸铋和载体，所述的生物炭和铁酸铋负载在载体上；所述生物炭和铁酸铋的重量比为1:30-15:2。2.根据权利要求1所述的基于美人蕉生物炭的废水处理材料，其特征在于：所述载体为海藻酸钙凝胶。3.一种基于美人蕉生物炭的废水处理材料的制备方法，其特征在于，包括以下步骤：1)美人蕉生物炭的制备，①将美人蕉叶片洗净，自然晾干至叶片变脆、打成粉末；②将步骤①的粉末转移到炭化装置中，在炭化装置中处于缺氧或者无氧条件下进行炭化；炭化温度为200-1000℃，保持1-5小时，升温速率为5-10℃/min；炭化装置冷却到室温即得到美人蕉生物炭；2)称取1-10份海藻酸钠溶解在100-1000份超纯水中进行水浴加热，水浴温度为50-100℃；3)加入1-15份60-200目的铁酸铋粉末和2-30份步骤1)制备的美人蕉生物炭，恒温磁力搅拌20-60min直到混合均匀；4)将步骤3)的混合溶液滴加到质量浓度为1～10％的CaCl2溶液中，反应12小时以上，得到大小均匀的复合材料小球。4...
【专利技术属性】
技术研发人员：胡新将，周亦辰，谢广玉，赵运林，邱国强，汤春芳，霍惠雯，陈芳旭，
申请(专利权)人：中南林业科技大学，
类型：发明
国别省市：湖南,43