一种奥氏体不锈钢清洗钝化剂制造技术

本发明专利技术公开了一种奥氏体不锈钢清洗钝化剂，其是由如下质量百分比的原料组成：柠檬酸30‑40％、乙二胺四乙酸二钠0.1‑1％、羟基乙叉二磷酸(HEDP)1‑5％、羟基乙酸3‑8％、磷酸3‑8％、非离子表面活性剂0.1‑2％、322H 0.5‑3％、十二烷基苯磺酸钠0.5‑1％、硝酸钇0‑0.5％、缓蚀剂0.1‑1％、余量水。本发明专利技术制得的脱脂除锈钝化剂具有环保、无刺激性气味、无毒性的特点，能显著降低对人员和环境的危害，并有效降低生产成本。

A Cleaning Passivator for Austenitic Stainless Steel

The invention discloses an austenitic stainless steel cleaning passivator, which is composed of 30 40% citric acid, 0.1 1% ethylenediaminetetraacetic acid disodium, 1 5% hydroxyethylene diphosphate (HEDP), 3 8% phosphoric acid, 0.1 2% nonionic surfactant, 322H 0.5 3%, 0.5 1% sodium dodecylbenzenesulfonate and 0.1% yttrium nitrate. 0.5%, corrosion inhibitor 0.1%, residual water. The degreasing and rust removing passivator prepared by the invention has the characteristics of environmental protection, non-irritating odor and non-toxicity, can significantly reduce the harm to people and the environment, and effectively reduce the production cost.

【技术实现步骤摘要】
一种奥氏体不锈钢清洗钝化剂
本专利技术涉及不锈钢表面处理
，具体涉及一种奥氏体不锈钢清洗钝化剂。
技术介绍
奥氏体不锈钢具有优良的耐腐蚀性能、耐高温性能、耐低温性能等特性，用途非常广泛，是国民经济各部门发展的重要钢铁材料之一。奥氏体不锈钢在宇航、原子能、海洋开发、石油化工、食品加工、医药卫生、家用电器、厨房器皿等行业得到了广泛的应用。不锈钢制品的耐腐蚀性能主要取决于其表面形成的钝化膜的质量，如果钝化膜不完整或有缺陷，不锈钢制品的耐腐蚀性能就会降低。工程上通常对不锈钢制品进行酸洗、钝化处理，处理后的制品表面形成一层均匀、致密的钝化膜，使之光亮洁白。从而提高不锈钢制品的表面防腐质量，延长制品的使用寿命。不锈钢设备与部件在成形、组装、焊接、焊缝检查(如探伤、耐压试验)及施工标记等过程中带来表面油污、铁锈、非金属污物、低熔点金属污染物、油漆、焊渣与飞溅物等。这些污染物不仅影响不锈钢设备与部件的表面质量，而且破坏了其表面的钝化膜，降低了不锈钢的耐腐蚀性能。为了提高不锈钢的外观和耐蚀性，加工后的不锈钢设备与部件必须进行脱脂(清洗)、除锈(酸洗)和钝化处理。不锈钢表面脱脂、除锈与钝化，除最大本文档来自技高网...

【技术保护点】
1.一种奥氏体不锈钢清洗钝化剂，其特征在于，其是由如下质量百分比的原料组成：柠檬酸30‑40％、乙二胺四乙酸二钠0.1‑1％、羟基乙叉二磷酸(HEDP)1‑5％、羟基乙酸3‑8％、磷酸3‑8％、聚丙烯酸钠2‑6％、非离子表面活性剂0.1‑2％、322H 0.5‑3％、十二烷基苯磺酸钠0.5‑1％、硝酸钇0‑0.5％、缓蚀剂0.1‑1％、余量水。

【技术特征摘要】
1.一种奥氏体不锈钢清洗钝化剂，其特征在于，其是由如下质量百分比的原料组成：柠檬酸30-40％、乙二胺四乙酸二钠0.1-1％、羟基乙叉二磷酸(HEDP)1-5％、羟基乙酸3-8％、磷酸3-8％、聚丙烯酸钠2-6％、非离子表面活性剂0.1-2％、322H0.5-3％、十二烷基苯磺酸钠0.5-1％、硝酸钇0-0.5％、缓蚀剂0.1-1％、余量水。2.根据权利要求1所述的一种奥氏体不锈钢清洗钝化剂，其特征在于：所述不锈钢清洗钝化剂在20-45℃范围内...