The invention relates to a heat dissipation coating primer, which is made from the following raw materials: epoxy resin: 20%25%; amino resin: 4%5%; solvent: 20%35%; silicon carbide: 5%20%; anti-sedimentation powder: 1%1.5%; titanium dioxide: 5%15%; magnesium oxide: 5%; butyl ester: 2%; 20%; flake reinforcement filler: 6%15%; pigments. 15%-25%; coupling agent 0.5%-3%; dispersant 0.5%-1%; leveling agent 0.5%-1%. The invented epoxy resin has strong adhesion to metals, and can make the coating not easy to drop paint. The coupling agent can anchor the filler to the resin and the resin to the metal surface, enhance the adhesion of the paint film, and reasonable material proportion can make the primer have the characteristics of strong heat dissipation and adhesion.
【技术实现步骤摘要】
一种散热涂料底漆
本专利技术涉及一种散热涂料底漆，具体是涉及一种散热涂料底漆。
技术介绍
散热绝缘涂料是特殊功能涂料的一种，在电器、电子、机械设备、灯具等方面有着广泛的应用。现有的散热绝缘涂料种类较多，但其的散热能力不够强、容易掉漆。
技术实现思路
本专利技术要解决的技术问题是克服现有技术散热绝缘涂料散热能力不够强、容易掉漆的缺陷，提供一种散热涂料底漆。为解决上述技术问题，本专利技术提供以下技术方案：一种散热涂料底漆，按照重量百分比数计算，包括以下原料制成：环氧树脂：20％-25％；氨基树脂：4％-5％；溶剂：20％-35％；碳化硅：5-20％；防沉粉：1％-1.5％；钛白粉：5-15％；氧化镁：5-20％；丁酯:2-20％；片状增强填料：6％-15％；颜料：15％-25％；偶联剂0.5-3％；分散剂：0.5％-1％；流平剂：0.5％-1％。进一步的，所述颜料金红石型钛白粉。进一步的，所述分散剂为LH9010、LH163和LH120的混合物。本专利技术与现有技术相比具有的有益效果是：一种散热涂料底漆，环氧树脂对金属具有较强的粘附力密着性，可使涂层不容易掉漆，偶联剂起到填料与树脂及树脂与金属表面的锚定效果，增强漆膜的密着粘结力，合理的材料比例可使底漆具有散热能力强、附着力强等特点。具体实施方式实施例1按照重量百分比数计算，包括以下原料制成：环氧树脂：20％-25％；氨基树脂：4％-5％；溶剂：20％-35％；碳化硅：5-20％；防沉粉：1％-1.5％；钛白粉：5-15％；氧化镁：5-20％；丁酯:2-20％；片状增强填料：6％-15％；颜料：15％-25％；偶联...
【技术保护点】
1.一种散热涂料底漆，其特征在于：按照重量百分比数计算，包括以下原料制成：环氧树脂：20％‑25％；氨基树脂：4％‑5％；溶剂：20％‑35％；碳化硅：5‑20％；防沉粉：1％‑1.5％；钛白粉：5‑15％；氧化镁：5‑20％；丁酯:2‑20％；片状增强填料：6％‑15％；颜料：15％‑25％；偶联剂0.5‑3％；分散剂：0.5％‑1％；流平剂：0.5％‑1％。
【技术特征摘要】
1.一种散热涂料底漆，其特征在于：按照重量百分比数计算，包括以下原料制成：环氧树脂：20％-25％；氨基树脂：4％-5％；溶剂：20％-35％；碳化硅：5-20％；防沉粉：1％-1.5％；钛白粉：5-15％；氧化镁：5-20％；丁酯:2-20％；片状增强填料：6％-15％；颜料：15％-25％...
【专利技术属性】
技术研发人员：张义坤，张磊和，
申请(专利权)人：安徽友瓷化工科技有限公司，
类型：发明
国别省市：安徽,34