The utility model discloses an iron mould covered sand box with partial exhaust in the middle part. The parting surface is provided with an exhaust sheet connected with the outside of the sand box, a convex platform is set in the sealing area of the cavity between the inner mould cavities of the sand box, a sealing area is set around the convex platform, and a hole is drilled on the convex platform to pass through the outside of the sand box. After closing the box, the convex platform can exhaust through the exhaust hole; the convex platform is 0.5_2 mm lower than the parting surface. The iron mould sand-covered sand box with partial exhaust in the middle part of the utility model strengthens the exhaust of the iron mould sand-covered process in the pouring process and effectively reduces the defects of the casting such as blowhole.
【技术实现步骤摘要】
一种中间部位局部排气的铁模覆砂砂箱
本技术属于铁模覆砂造型工艺
,特别涉及一种中间部位局部排气的铁模覆砂砂箱。
技术介绍
一直以来,排气困难一直是铁模覆砂造型工艺的一个难题,原因在于其外部砂箱一般是铁质,铁没有透气性,而在实际生产浇注过程中,覆膜砂受热后发气会导致很多问题,比如浇注充型困难,铸件气孔缺陷严重等。现有的大多数排气设计在砂箱的边缘会增加排气片,排气片的厚度一般在0.1mm-0.15mm,这样才可以保证造型时不会跑砂,然而在某些情况下,特别是砂箱中间部位的排气不能满足要求,如一模多腔的产品,排列在四周靠近边缘的位置可以排气,排列在中间部位的排气就不好。
技术实现思路
此技术的目的是在砂箱中部增加排气设计,保证一些排列在中部的模腔也可以排气,降低气孔的废品率。本技术的目的是采用以下技术方案实现的,一种中间部位局部排气的铁模覆砂砂箱,分型面上设有连通砂箱外部的排气片,在砂箱内模腔之间的型腔密封区内设立凸台,凸台周围设置密封区,在凸台上钻有孔直通砂箱外部,合箱后可以通过此排气孔排气。优选地,所述凸台比分型面低0.5-2mm。本技术中间部位局部排气的铁模覆砂砂箱,加强铁模覆砂工艺在浇注过程中排气,有效降低铸件气孔等缺陷。附图说明图1是本技术实施例的一种中间部位局部排气的铁模覆砂砂箱的结构示意图。具体实施方式下面结合附图详细介绍本技术技术方案。图1所示是本技术中间部位局部排气的铁模覆砂砂箱的一个实施例,如图1所示,对于中间5号模腔1、6号模腔8来说,距离砂箱边缘远,排气不顺畅。本技术在合适位置增加凸台2,凸台比分型面低0.5-2mm,其周围设置密封区,在凸台 ...
【技术保护点】
1.一种中间部位局部排气的铁模覆砂砂箱,分型面上设有连通砂箱外部的排气片,其特征在于,在砂箱内模腔之间的型腔密封区内设立凸台,凸台周围设置密封区,在凸台上钻有孔直通砂箱外部,合箱后可以通过此排气孔排气。
【技术特征摘要】
1.一种中间部位局部排气的铁模覆砂砂箱,分型面上设有连通砂箱外部的排气片,其特征在于,在砂箱内模腔之间的型腔密封区内设立凸台,凸台周围设置密封区,在凸台...