The invention discloses an anti-mildew and anti-bacterial packaging bag material, whose raw materials include polypropylene, organic phosphorus-containing anti-mildew agent, plant anti-bacterial agent, nano-filler, coupling agent and stabilizer. Organic phosphorus-containing antifungal agent was prepared by adding alkyl primary amine and alkyl hypophosphite into solvent, stirring at elevated temperature, then adding cyanamide solution. After further reaction, the solvent was removed and dried to prepare the prefabricated material. After heating reflux reaction between the prefabricated material and N hydroxyethyl ethylenediamine, the organic phosphorus-containing antifungal agent was prepared. The packaging film material of the invention has good anti-mildew and anti-bacterial properties and excellent mechanical properties.
【技术实现步骤摘要】
一种防霉抗菌包装袋材料
本专利技术涉及包装膜袋
，尤其涉及一种防霉抗菌包装袋材料。
技术介绍
塑料包装材料是以合成或天然的高分子树脂为主要材料，添加各种助剂后，在一定的温度和压力下具有延展性，冷却后可以固定其形状的一类材料。塑料的主要特性是:第一，密度小，比强度高，可以获得较高的包装得率；第二，大多数塑料的耐化学性好，有良好的耐酸，耐碱，耐各类有机溶剂，长期放置，不发生氧化；第三，成型容易，所需成型能耗低于钢铁等金属材料；第四，具有良好的透明性，易着色性；第五，具有良好的强度，单位重量的强度性能高，耐冲击，易改性；第六，加工成本低。第七，绝缘性优。然而目前，塑料包装袋使用过程中以滋生霉菌，不能满足需求。
技术实现思路
基于
技术介绍
存在的技术问题，本专利技术提出了一种防霉抗菌包装袋材料，防霉抗菌性能好，力学性能优异。本专利技术提出一种防霉抗菌包装袋材料，其原料按重量份包括：聚丙烯80-100份，有机含磷防霉剂5-15份，植物抗菌剂1-3份，纳米填料4-10份，偶联剂1-3份，稳定剂0.5-2份。优选地，有机含磷防霉剂采用如下工艺制备：将烷基伯胺、烷基次磷酸加入溶剂...
【技术保护点】
1.一种防霉抗菌包装袋材料，其特征在于，其原料按重量份包括：聚丙烯80‑100份，有机含磷防霉剂5‑15份，植物抗菌剂1‑3份，纳米填料4‑10份，偶联剂1‑3份，稳定剂0.5‑2份。
【技术特征摘要】
1.一种防霉抗菌包装袋材料，其特征在于，其原料按重量份包括：聚丙烯80-100份，有机含磷防霉剂5-15份，植物抗菌剂1-3份，纳米填料4-10份，偶联剂1-3份，稳定剂0.5-2份。2.根据权利要求1所述防霉抗菌包装袋材料，其特征在于，有机含磷防霉剂采用如下工艺制备：将烷基伯胺、烷基次磷酸加入溶剂中，升温搅拌反应，再加入氰胺溶液，继续反应后，脱溶剂、干燥制得预制料；将预制料与N-羟乙基乙二胺加热回流反应后，制得有机含磷防霉剂。3.根据权利要求2所述防霉抗菌包装袋材料，其特征在于，烷基伯胺、烷基次磷酸、氰胺、N-羟乙基乙二胺的摩尔比为5-6：7-8：5-6：2-3。4.根据权利...