The invention discloses a method for preparing a hydrogel with hierarchical structure and the obtained hydrogel, in which a certain concentration of chitosan is added to a centrifugal tube, a certain concentration of xanthan gum solution is added to the top of the chitosan solution, and the hydrogel with hierarchical structure is formed after a period of spontaneous interfacial diffusion reaction. At the same time, the gel has hierarchical structure. At the same time, because of its good biocompatibility, safety and biodegradability, it is an ideal material for preparing hydrogels, and can be used in medical biomaterials and drug carriers. It has good prospects for research and development.
【技术实现步骤摘要】
一种制备具有分级层次结构水凝胶的方法及得到的水凝胶
本专利技术涉及水凝胶领域，具体涉及具有分级层次结构的水凝胶制备。
技术介绍
水凝胶是一种具有亲水性的三维网状交联结构的高分子网络体系。水凝胶性质柔软，能保持一定的形状，能吸收大量的水，具有良好的生物相容性和生物降解性，因此，被应用于组织工程、药物输送、3D细胞培养等医药学领域。但是，在现有技术中，大多涉及的是普通水凝胶，多层结构的水凝胶涉及较少，尤其是具有分级层次结构的水凝胶研究更少。
技术实现思路
本专利技术人进行了锐意研究，利用壳聚糖和黄原胶的界面反应，得到一种具有分级层次结构的水凝胶，其中，所述水凝胶具有独特的三层结构，在组织工程和生物领域有广泛的应用；同时，所述制备工艺简单、环保，制备成本低且适于规模化生产。本专利技术的目的之一在于提供一种制备具有分级层次结构水凝胶的方法，具体体现在以下几个方面：(1)一种制备具有分级层次结构水凝胶的方法，其中，所述方法包括以下步骤：步骤1、将壳聚糖加入水中，得到壳聚糖溶液；步骤2、将黄原胶加入水中，得到黄原胶溶液；步骤3、依次将步骤1得到的壳聚糖溶液和步骤2得到的黄原胶溶液...
【技术保护点】
1.一种制备具有分级层次结构水凝胶的方法，其特征在于，所述方法包括以下步骤：步骤1、将壳聚糖加入水中，得到壳聚糖溶液；步骤2、将黄原胶加入水中，得到黄原胶溶液；步骤3、依次将步骤1得到的壳聚糖溶液和步骤2得到的黄原胶溶液加入到容器(例如离心管)中，在界面处进行反应，得到所述具有分级层次结构的水凝胶。
【技术特征摘要】
1.一种制备具有分级层次结构水凝胶的方法，其特征在于，所述方法包括以下步骤：步骤1、将壳聚糖加入水中，得到壳聚糖溶液；步骤2、将黄原胶加入水中，得到黄原胶溶液；步骤3、依次将步骤1得到的壳聚糖溶液和步骤2得到的黄原胶溶液加入到容器(例如离心管)中，在界面处进行反应，得到所述具有分级层次结构的水凝胶。2.根据权利要求1所述的方法，其特征在于，在步骤1中，所述壳聚糖的分子量为2000～10000Da，优选为2000～6000Da，更优选为2000～4000Da(例如2000～3000Da)。3.根据权利要求1或2所述的方法，其特征在于，在步骤2中，所述黄原胶的分子量为200000～800000Da，优选为300000～700000Da，更优选为400000～600000Da。4.根据权利要求1至3之一所述的方法，其特征在于，在步骤1所述的壳聚糖溶液中，壳聚...
【专利技术属性】
技术研发人员：隋坤艳，潘娜，崔慧琳，谭业强，范汶鑫，张肖辉，高旭冉，
申请(专利权)人：青岛大学，
类型：发明