本发明专利技术提供了一种以间苯二酚杯芳烃（Calix[4]resorcinarene,CRA）为核的星形发光材料及其在有机电致发光器件中的应用，该类化合物合成方法简单、反应条件温和且产率较高。特别是核体CRA有八个高反应活性位点，可以挂接八个功能基团，相应的功能化合物具有较好的成膜性、溶解性和较高的热稳定性。本发明专利技术化合物作为发光层材料应用于有机电致发光器件，可以获得优异的器件性能。

A resorcinol calixarene compound and its preparation method and Application

The invention provides a star-shaped luminescent material with resorcinarene (CRA) as core and its application in organic light-emitting devices. The synthesis method of the compound is simple, the reaction conditions are mild and the yield is high. In particular, the nucleosome CRA has eight highly reactive sites, which can be linked to eight functional groups. The corresponding functional compounds have good film-forming, solubility and high thermal stability. The compound of the invention can be used as a light-emitting layer material in organic electroluminescent devices and obtain excellent device performance.

【技术实现步骤摘要】
一种间苯二酚杯芳烃化合物及制备方法与应用
本专利技术属于有机光电材料
，尤其涉及一种间苯二酚杯芳烃化合物及制备方法与应用。
技术介绍
OLED是采用有机物作为发光材料的器件。具有驱动电压低、发光亮度和发光效率高、响应速度快、视角宽、生产工艺简单等优点，越来越多地用于显示器来取代传统的液晶显示器。传统的底发射型OLED是由附着在玻璃基底上的透明阳极氧化铟锡(IndiumTinOxide,ITO)，有机功能层(多层)和反射阴极Al(或其它阴极材料)组成的。另外，将反射阴极更换为具有一定透明度的电极材料，则可获得顶发射型OLED或者透明OLED。在电激发条件下，空穴和电子分别从正极和负极注入到发光层，发光分子吸收能量受激发跃迁到高能级而形成单重态和三重态激子，激子再通过辐射发出可见光。传统的荧光材料只能利用单重态激子进行辐射发光，理论最大内量子效率仅为25％。磷光材料通过引入贵金属，可以同时利用单重态和三重态激子进行辐射发光，理论最大内量子效率为100％，不过存在贵金属的稀缺、成本高、对环境污染等缺点。基于这种需要，热活化延迟荧光(ThermallyActivatedDelayedF本文档来自技高网...

【技术保护点】
1.一种间苯二酚杯芳烃化合物，其特征在于，所述化合物的结构如通式(1)所示：

【技术特征摘要】
2018.10.10 CN 20181117931701.一种间苯二酚杯芳烃化合物，其特征在于，所述化合物的结构如通式(1)所示：其中，A1-A8为八个活性位点与功能成分反应后形成的官能团，R1-R8为有机发光二极管发光材料。2.如权利要求1所述的间苯二酚杯芳烃化合物，其特征在于，A1-A8为1,4-二取代-1,2,3-三氮唑基团，其结构为3.如权利要求1所述的间苯二酚杯芳烃化合物，其特征在于，R1-R8选自以下任一种基团：4.权利要求1-3任一所述的间苯二酚杯芳烃化合物在有机电致发光材料中的应用。5.如权利要求4所述的间苯二酚杯芳烃化合物在有机电致发光材料中的应用，其特征在于，所述间苯二酚杯芳烃化合物为OLED发光层。6.一种含有权利要求1-3中任一所述的间苯二酚杯芳烃化合物的有机电致发光器件。7.如权利要求6所述的有机电致发光器件，其特征在于，其结构为：ITO/PEDOT:PSS/Poly-TPD/PVK/发光层/TmP...