The invention provides a high performance alloy slag concrete and its preparation method, which is made of 13-15 portions of cement, 5-7 portions of alloy slag, 1-3 portions of ore powder, 5-7 portions of water, 50 portions of sand and stone, 0.5-1.5 portions of carbon fiber composite material, 3-6 portions of additives, 1-3 portions of aluminium chloride, 1-3 portions of aluminium oxide, 2-4 portions of potassium hydroxide, 6-8 portions of urea, 3-7 portions of N-methylpyrrolidone. This paper mainly overcomes the shortcomings of low compressive strength and poor flexural strength of concrete, and provides a preparation method of high performance alloy slag concrete with simple preparation technology. The high performance alloy slag concrete has the advantages of light weight, high strength and high toughness, and is expected to be directly applied to batch industrial production in the future.
【技术实现步骤摘要】
一种高性能合金渣混凝土及其制备方法
本专利技术属于建筑材料领域,具体涉及一种高性能合金渣混凝土及制备方法。
技术介绍
随着现代建筑技术的不断发展,对水泥混凝土提出了更高的要求,它正朝着高强度、高韧性、高阻裂、高耐久性、高体积稳定性和优良的工艺性的方向发展。然而,混凝土在使用过程中,特别是拉应力存在条件下,易产生裂纹而最终导致材料和结构的完全破坏。因此,混凝土的强韧化多年来一直是力学界和材料学界致力研究的跨学科的难题。国内外关于钢纤维混凝土的研究和应用最为成熟。但有研究表明,钢纤维对混凝土的抗压强度并无明显促进作用,甚至还有所降低;与素混凝土相比,对于钢纤维混凝土的抗渗性、耐磨性、耐冲磨性及对防止混凝土早期塑性收缩等还存在正反(提高与降低)两方面甚至居中的观点。此外,钢纤维混凝土用量较大、价格较高,有生锈问题,对由于火灾引起的爆裂几乎无效等,这些问题都在不同程度影响了其应用。因此,专利技术一种合适形式的纤维混凝土迫在眉睫。现代混凝土除了要达到高抗压、高抗拉等要求外,还要容易施工,并且保持高强、高韧性等性能。因此纤维高性能合金渣混凝土在混凝土的改性过程中应运而生。与此 ...
【技术保护点】
1.一种高性能合金渣混凝土,其特征在于由,该混凝土由如下重量份的原料制备而成:水泥13~15份、合金渣5~7份、矿粉1~3份、水5~7份、砂石50份、碳纤维复合材料0.5~1.5份、助剂3~6份、氯化铝1~3份、氧化铝1~3份、氢氧化钾2~4份、尿素6~8份、N‑甲基吡咯烷酮3~7份。
【技术特征摘要】
1.一种高性能合金渣混凝土,其特征在于由,该混凝土由如下重量份的原料制备而成:水泥13~15份、合金渣5~7份、矿粉1~3份、水5~7份、砂石50份、碳纤维复合材料0.5~1.5份、助剂3~6份、氯化铝1~3份、氧化铝1~3份、氢氧化钾2~4份、尿素6~8份、N-甲基吡咯烷酮3~7份。2.根据权利要求1所述的混凝土,其特征在于由,该混凝土由如下重量份的原料制备而成:水泥14份、合金渣6份、矿粉2份、水6份、砂石50份、碳纤维复合材料1份、助剂4.5份、氯化铝2份、氧化铝2份、氢氧化钾3份、尿素7份、N-甲基吡咯烷酮5份。3.根据权利要求1或2所述的混凝土,其特征在于,所述碳纤维复合材料是将碳纤维在环氧树脂中浸润,得叠层湿法预浸料,...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。