The invention discloses a multi-layer gradient cemented carbide punch. The first cemented carbide punch comprises a first cemented carbide layer at the top of the punch and a second cemented carbide layer at the inner side of the first cemented carbide layer. The ratio of the thickness of the first cemented carbide layer to the thickness of the second cemented carbide layer is 1:3 9:11. The composition of the first cemented carbide layer includes tungsten carbide and cobalt, and the weight percentage of the cobalt is 4%8%. The composition of the second cemented carbide layer includes tungsten carbide and cobalt, and the weight percentage of the cobalt is 8%-16%. The multi-layer gradient cemented carbide punch has high body strength and high wear resistance at the top of the punch.
【技术实现步骤摘要】
一种多层梯度硬质合金冲头
本专利技术涉及硬质合金设备
，更具体地，涉及一种多层梯度硬质合金冲头。
技术介绍
硬质合金由于其高强度、高硬度、高耐磨性和高红硬性，被广泛的应用加工冲头、耐磨零件及矿山工具等。目前使用较多的柱齿冲头、楔形冲头等使用的硬质合金材料都是采用单种配方的原材料粉末制备的合金。这类单种配方原材料粉末制备的合金经高温烧结制备冲头，其冲头头部及冲头身部都是同一性能的合金。然而硬质合金冲头在工作中，其各部分所要求的性能，如硬度、耐磨性、抗弯强度、断裂韧性是不一样的，为了具有更高的耐磨性，冲头顶部必须有高硬度；为了防止断裂，冲头身部必须具有高抗弯强度和高断裂韧性的特点；冲头底部使用要求比较低。通常由单一晶粒度的硬质相和同一含量的粘结相烧结成的硬质合金冲头各部位的硬度、抗弯强度和断裂韧性相同，不能满足使用特性要求。因此，需要提供一种新的技术方案，以解决上述技术问题。
技术实现思路
本专利技术的一个目的是提供一种多层梯度硬质合金冲头的新技术方案。根据本专利技术的第一方面，提供了一种多层梯度硬质合金冲头。硬质合金冲头包括位于冲头顶部的第一硬质合金层和结合在所述...
【技术保护点】
1.一种多层梯度硬质合金冲头，其特征在于：包括位于冲头顶部的第一硬质合金层和结合在所述第一硬质合金层的内侧的第二硬质合金层，所述第一硬质合金层的厚度和所述第二硬质合金层的厚度之比为1:3‑9:11，所述第一硬质合金层的成分包括碳化钨和钴，所述钴的重量百分比为4％‑8％；所述第二硬质合金层的成分包括碳化钨和钴，所述钴的重量百分比为8％‑16％。
【技术特征摘要】
1.一种多层梯度硬质合金冲头，其特征在于：包括位于冲头顶部的第一硬质合金层和结合在所述第一硬质合金层的内侧的第二硬质合金层，所述第一硬质合金层的厚度和所述第二硬质合金层的厚度之比为1:3-9:11，所述第一硬质合金层的成分包括碳化钨和钴，所述钴的重量百分比为4％-8％；所述第二硬质合金层的成分包括碳化钨和钴，所述钴的重量百分比为8％-16％。2.根据权利要求1所述的多层梯度硬质合金冲头，其特征在于：所述第一硬质合金层的厚度为2-15mm；所述第二硬质合金层的厚度为6-25mm。3.根据权利要求1所述的多层梯度硬质合金冲头，其特征在于：所述第一硬质合金层和所述第二硬质合金层之间的接触界面为向所述第一硬质合金层内凹的第一球面。4.根据权利要求3所述的一种多层梯度硬质合金冲头，其特征在于：所述冲头顶部的外侧面为第二球面,所述第一...
【专利技术属性】
技术研发人员：毛咏发，张允继，俞胜平，
申请(专利权)人：歌尔股份有限公司，
类型：发明
国别省市：山东,37