The invention relates to a surface pretreatment neutralizing liquid for aluminium and aluminium alloys, which belongs to the technical field of metal surface treatment. The neutralizing solution is composed of oxidant, fluorine-containing compound, stabilizer, accelerator, acid, surfactant and water. It can effectively remove all kinds of harmful impurities and dirt after alkali etching treatment in the pretreatment process of aluminium and aluminium alloys containing or without silicon. The neutralizing effect is good and the quality is stable. It can form a uniform and activated surface, which is conducive to subsequent treatment. At the same time, it solves the problem that the traditional neutralizing solution contains a lot of nitric acid and hydrofluoric acid, which seriously pollutes the environment.
【技术实现步骤摘要】
一种铝表面预处理中和液
本专利技术属于铝表面前处理
，去除碱蚀处理后存在的各种有害杂质和污垢，而且能形成均匀而活化的表面，有利于后续处理。
技术介绍
铝合金密度小、比强度高，在航空、电子、汽车、建筑、轻工业等领域应用广泛。采用压铸技术可以高速生产精度高、形状复杂且重量轻的铝合金零部件。因此，压铸铝合金的使用量正逐年增加。由于硅和铜等元素的加入，使压铸成型铝合金零件耐蚀性明显降低，阳极氧化处理不易获得均匀的保护膜。另外，其表面硬度低，容易磨损，外表光泽不能保持太久，耐脏性、装饰性差。虽然有报道称铬酸盐技术是一种较好的铸铝合金表面处理方法，但由于六价铬在自然环境条件下不能自然分解，易在生物和人体内积聚而导致病变。因此，我国已于2007年3月1日起执行欧盟RoHS指令，禁止在转化处理过程中使用六价铬等有害物质。因此，研究开发铝和铝合金表面处理新技术、新工艺，有十分重要的意义。在铝及铝合金前处理工艺中，铝及铝合金经脱脂和碱蚀工序后，合金中的铁、锰、铜、镁、硅等不溶于碱，残留在工件表面上，形成一层灰黑色的疏松物质，影响后续工艺的进行，因此必须除去。工业生产过程中常用的方法是化学溶解法，亦即通常所说的中和，或称为酸洗。对于中和处理，国内外所用的工艺都比较简单，大多采用三酸、双酸或单酸(硝酸)处理。其目的不仅要去除碱蚀处理后产生的各种氧化物和污垢，而且能形成均匀而活化的金属表面，以利于后面的处理工艺的进行。但生产过程中普遍使用大量硝酸和氢氟酸，给生产车间、周围环境、工人健康和社会的可持续发展造成严重的影响。同时也存在中和质量的不稳定。鉴于铝合金表面预处理中中和处理...
【技术保护点】
1.一种铝表面预处理中和液，其特征在于，所述的中和液的组成和配比范围是：氧化剂：1‑600克/升；含氟化合物：1‑600克/升；稳定剂：0.01‑50克/升；促进剂：0‑30克/升；表面活性剂：0‑50克/升；酸：0‑200克/升；水余量。
【技术特征摘要】
1.一种铝表面预处理中和液，其特征在于，所述的中和液的组成和配比范围是：氧化剂：1-600克/升；含氟化合物：1-600克/升；稳定剂：0.01-50克/升；促进剂：0-30克/升；表面活性剂：0-50克/升；酸：0-200克/升；水余量。2.按照权利要求1的中和液，其特征在于：所述的氧化剂是过硫酸钾、过硫酸铵、过硫酸钠、过硫酸氢钠、过硫酸氢钾、过硼酸盐、过碳酸盐中的至少一种或者几种化合物的混合物。3.按照权利要求1的中和液，其特征在于：所述含氟化合物为氟化氢钾、氟化锂、氟化钠、氟化钾、氟化铵或氟化氢铵中的至少一种或几种化合物的混合物。4.按照权利要求1的...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。