The invention discloses a cable material, which comprises the following weight parts: crosslinked polyethylene: 90 100 copies, stearic acid: 10 12 copies, magnesium hydroxide: 50 80 copies, ultraviolet absorbent: 5 10 copies, coupling agent: 2 6 copies, stabilizer: 3 6 copies, plasticizer: 1 3 copies. The invention adopts halogen-free flame retardant, which can effectively reduce smoke, improve the processing performance and low smoke self-extinguishing performance of cable material, improve the anti-cracking performance and service life of products with ultraviolet absorbent, and has reasonable composition of raw materials, high flame retardant performance, low smoke and non-toxic when burning, and environmental protection.
【技术实现步骤摘要】
一种电缆料
本专利技术涉及电缆料
，尤其涉及一种电缆料。
技术介绍
随着社会的发展，高层建筑、重要建筑的防火越来越引起人们的重视，为提高防火安全等级，大多会采用阻燃电缆或耐火电缆。为了防止电缆失火，必须要提高电缆料的阻燃性能、降低其燃烧性，减缓燃烧速度，一般是在高分子材料中添加一定的阻燃剂。目前的电缆料大多含有卤，燃烧时释放出大量烟雾和有毒的、腐蚀性的气体，对环境与人体造成严重的伤害。此外架在空中的电缆常常会受到紫外线的侵蚀，使得电缆过早的龟裂，影响电缆的电缆输送。
技术实现思路
专利技术目的：为了克服现有技术中存在的不足，提供一种电缆料，阻燃性能高，燃烧时低烟，无卤，环保，而且具有抗紫外线功能。技术方案：为实现上述目的，本专利技术提供一种电缆料，包括以下重量份的原料：交联聚乙烯：90-100份，硬脂酸：10-12份，氢氧化镁：50-80份，紫外线吸收剂：5-10份，偶联剂：2-6份，稳定剂：3-6份，增塑剂：1-3份。进一步地，所述偶联剂为硅烷偶联剂。进一步地，所述稳定剂为环保钙锌稳定剂。进一步地，所述增塑剂为石蜡和/或偏苯三酸三辛酯。有益效果：本专利技术与现...
【技术保护点】
1.一种电缆料，其特征在于，包括以下重量份的原料：交联聚乙烯：90‑100份，硬脂酸：10‑12份，氢氧化镁：50‑80份，紫外线吸收剂：5‑10份，偶联剂：2‑6份，稳定剂：3‑6份，增塑剂：1‑3 份。
【技术特征摘要】
1.一种电缆料，其特征在于，包括以下重量份的原料：交联聚乙烯：90-100份，硬脂酸：10-12份，氢氧化镁：50-80份，紫外线吸收剂：5-10份，偶联剂：2-6份，稳定剂：3-6份，增塑剂：1-3份。2.根据权利要...