The invention discloses an ultraviolet high transmittance and low refractive index glass for light transmission rod. The ultraviolet high transmittance and low refractive index glass for light transmission rod comprises the following components according to weight percentage: B2O 3 0-23%, SiO 2 60-75%, AlO 3 0.5-9%, NaO 0-12%, KO 1-15%, CaO 0-8%, ZnO 0-3%. The glass of the invention has good crystallization resistance and chemical stability, and the ultraviolet spectral transmittance of the glass is more than 90% under the control of 5 + 1 mm thickness. The melted glass has no stone and high gloss. The softening temperature is controlled at 550 650 and no crystallinity is produced after holding at 850 for 2 hours.
【技术实现步骤摘要】
一种用于传光棒的紫外高透过率低折射率玻璃本专利技术涉及玻璃制备
，具体涉及一种用于传光棒的280-380nm紫外高透过率低折射率玻璃。
技术介绍
传光棒是由成千上万根光学纤维不规则排列、加热、拉制制成的棒状纤维束。其中每一根纤维均由高折射率芯玻璃和低折射率包皮玻璃构成，并依据光学全反射原理进行光单向传递。传光棒主要用于紫外光固化机，对300-380mm紫外光有很高透过率，从而实现对紫外固化剂的光固化。传光棒是由低折射率的皮料和高折射率的芯料经过管棒法组合拉纤维，并合成纤维束拉制成棒状串光纤维束而制成。传光棒利用了光在高折射率芯料和低折射率皮料之间的全反射而向前传播光能。它与光纤面板不同之处在于，光纤面板是规则排列的传光传像纤维板，而传光棒为不规则排列的传光纤维板。制作工艺相类似，产品应用不同。根据传光棒产品技术要求：300-380nm的透过率≥85%，有很好的紫外光透过性能。此外，在传光棒的制造过程中，低折射率玻璃要求与高折射率芯料粘度匹配；软化温度范围550-650℃；析晶下限温度≥850℃，抗析晶能力强，化学稳定性好。普通的光学玻璃，在5mm厚度控制下可见光范...
【技术保护点】
1.一种用于传光棒的280‑380nm紫外高透过率低折射率玻璃，其特征在于所述用于传光棒的紫外高透过率低折射率玻璃包括按照重量百分比的如下组分组成：B2O3 0~23%，SiO2 60~75%，Al2O3 0.5~9%，Na2O 0~12%，K2O 1~15%，CaO 0~8%，ZnO 0~3%，BaO 0~3%。
【技术特征摘要】
1.一种用于传光棒的280-380nm紫外高透过率低折射率玻璃，其特征在于所述用于传光棒的紫外高透过率低折射率玻璃包括按照重量百分比的如下组分组成：B2O30~23%，SiO260~75%，Al2O30.5~9%，Na2O0~12%，K2O1~15%，CaO0~8%，ZnO0~3%，BaO0~3%。2.根据权利要求1所述的用于传光棒的紫外高透过率低折射率玻璃，其特征在于所述用于传光棒的紫外高透过率低折射率玻璃还包括按照重量百分比的如下组分组成：Sb2O30~1%。3.权利要求1所述的用于传光棒的280-380nm紫外高透过率低折射率玻璃的制备方法，其特征在于包括如下步骤：（1）在温度为1380-1400℃下，将各原料加入铂金坩埚窑中；（2）加料完成后用时60-90min升温至澄清温度1450±10℃，澄清时间为8-10h；...
【专利技术属性】
技术研发人员：朱思锋，徐士强，朱海英，王斌，
申请(专利权)人：杭州富阳环宇玻璃厂，
类型：发明
国别省市：浙江,33