The invention provides a method for preparing an air electrode, which includes: (1) forming a first diffusion layer and a second diffusion layer on both sides of the collector; (2) preparing a spinning solution from catalyst and polymer solution; (3) spraying the spinning solution on the first diffusion layer to obtain a catalytic layer; (4) placing a waterproof breathable film on the second diffusion layer, and rolling to obtain the air electrode. The air electrode prepared by the preparation method of the air electrode provided by the invention has strong conductivity, good permeability and high catalytic performance, which can slow down the polarization phenomenon of the air battery and improve the electrochemical performance of the battery.
【技术实现步骤摘要】
空气电极的制备方法
本专利技术属于空气电池
，具体涉及一种空气电极的制备方法。
技术介绍
空气电极是一种气体扩散电极，其一面与电解质接触，一面与空气中的氧气接触，在催化剂表面形成一种三相稳定的状态。在电池放电过程中，空气电极作为阴极，氧气沿电极表面扩散进入电极内部，在催化剂的作用下发生还原反应。空气电极性能的优劣除与催化剂有关之外，还与空气电极的结构相关，要求空气电极具有高孔隙率、孔分布均匀、透气性好，同时具有良好防渗透能力。目前，空气电极多存在极化现象，催化剂和氧气在阴极催化剂结构中不能形成良好的三相反应界面，而不利于反应产物的扩散和转移，导致反应产物的沉积而阻碍氧气在催化剂中的扩散，同时由于反应产物的导电性较差而增大了空气电池的电化学极化，进而过高的充电电压将分解电池体系中的有机电解液而致使空气电池不能正常工作。此外，空气电池的结构也会影响极化程度，高孔隙率、透气性较好的空气电池会提升催化剂的性能，从而提升电池的电化学性能，减缓空气电池极化的发生。因此，亟需提供一种高孔隙率、透气性好且催化性能高的空气电极的制备方法。
技术实现思路
本专利技术的目的在于提供一...
【技术保护点】
1.一种空气电极的制备方法，其特征在于，包括：(1)在集流体两侧形成第一扩散层和第二扩散层；(2)将催化剂与高分子溶液配成纺丝液；(3)将所述纺丝液喷涂在所述第一扩散层上得到催化层；(4)将防水透气膜放置在所述第二扩散层上，辊压得到所述空气电极。
【技术特征摘要】
1.一种空气电极的制备方法，其特征在于，包括：(1)在集流体两侧形成第一扩散层和第二扩散层；(2)将催化剂与高分子溶液配成纺丝液；(3)将所述纺丝液喷涂在所述第一扩散层上得到催化层；(4)将防水透气膜放置在所述第二扩散层上，辊压得到所述空气电极。2.如权利要求1所述的空气电极的制备方法，其特征在于，步骤(1)中，将活性炭和聚四氟乙烯混合配置，渗透在所述集流体的两侧，得到所述第一扩散层和所述第二扩散层。3.如权利要求1所述的空气电极的制备方法，其特征在于，步骤(2)中，所述催化剂选自碳载铂、碳载银和碳载二氧化锰中的一种或多种。4.如权利要求1所述的空气电极的制备方法，其特征在于，步骤(2)中，所述高分子溶液选自PVA或PVP。5.如权利要求1所述的空气电极的制备方法，其特征在于，步骤(2)中，所述催化剂与所述高分子溶液的质量比为1:1～10。6.如权利要求1所述的空...
【专利技术属性】
技术研发人员：夏德兴，李宁，呼继梅，
申请(专利权)人：东莞市中航华讯卫星技术有限公司，
类型：发明
国别省市：广东,44