The invention discloses a cobalt complex catalyst and a carbon nanotube/cobalt complex composite catalyst and its application. A carbon nanotube/molecule catalyst (CNTs/Co(salophen)) composite catalyst was prepared by using molecule-level cobalt complex Co(salophen) with stable structure as catalyst. The cobalt complex catalyst was decomposed into corresponding water/hydroxyl complexes and free ligands under strong acid and alkaline conditions. CNTs/Co(salophen) composite catalyst was prepared by nafion. The composite cathode designed by the invention not only greatly improves the catalytic activity of the catalyst, but also realizes the electrocatalytic reduction of carbon dioxide by the composite cathode of heterogeneous catalyst driven by an applied voltage.
【技术实现步骤摘要】
一种钴配合物催化剂及碳纳米管/钴配合物复合催化剂和应用
本专利技术属于电催化领域，特别涉及一种钴配合物催化剂及碳纳米管/钴配合物复合催化剂
技术介绍
当今，人类面临着两大难题：大气中CO2含量不断升高而导致全球温室效应；燃料资源日益匮乏。充分利用自然界富有的CO2进行转化和固定，不仅有利于消除大气温室效应，又能生成有机燃料，合成其它有机化工原料、中间体或有机化工产品，同时可以减少由其它化工原料反应而带来的环境污染问题。所以，CO2的综合利用具有化学反应绿色化、积极保护环境的重要意义。由于电催化CO2还原反应可以应用电将二氧化碳消除，而其体系简便易控，因此正成为人们研究的一个重要方向。早期的研究，主要是以Ru，Ir等贵金属单质及相应的氧化物，配合物为分子催化剂，在均相体系中实现二氧化碳的还原。经过近十年的研究，二氧化碳还原从最初的化学催化体系逐渐发展到电催化体系和光电化学电池等多种反应体系。与传统的金属氧化物多相催化剂相比，许多分子水平的二氧化碳还原催化剂在催化活性以及结构可调性上，有明显优势。因此研究非均相催化体系的分子水平的二氧化碳还原催化剂具有实际意义。专利技...
【技术保护点】
1.钴配合物催化剂，其特征在于，所述的钴配合物催化剂为Co(salophen)，具有如(I)所示的结构式：
【技术特征摘要】
1.钴配合物催化剂，其特征在于，所述的钴配合物催化剂为Co(salophen)，具有如(I)所示的结构式：2.权利要求1所述的钴配合物催化剂的制备方法，其特征在于，包括如下步骤：1)salophen配体的制备：于乙醇中加入水杨醛和邻苯二胺，在70-80℃下加热回流反应6-7h，反应完全后，将溶液冷却至室温后减压蒸馏并抽滤，然后真空干燥12小时，得salophen配体；2)钴配合物催化剂Co(salophen)的制备：在氮气保护下，于乙醇中加入salophen配体和Co(OAc)2·4H2O，在70-80℃下加热回流反应2-3h，反应液冷却至室温后，乙醇洗涤，抽滤，真空干燥，得钴配合物催化剂Co(salophen)。3.根据权利要求2所述的钴配合物催化剂的制备方法，其特征在于，按摩尔比，邻苯二胺：水杨醛＝1:2；salophen配体：Co(OAc)2·4H2O＝1:1.2。4.一种碳纳米管/钴配合物复合催化剂，其特征在于，是将权利要求1所述的钴配合物催化剂Co(salophen)与碳纳米管CNTs复合，构成的碳纳米管/钴配合物复合催化剂CNTs/Co(salophen)。5.权利要求4所述的一种碳...
【专利技术属性】
技术研发人员：夏立新，徐英明，姜毅，张谦，
申请(专利权)人：辽宁大学，
类型：发明
国别省市：辽宁,21