The invention discloses a foam concrete Luqiao filling material, which belongs to the technical field of building materials. It includes 100 portions of cement, 10-15 portions of fly ash, 5-10 portions of gangue ceramsite, 20-30 portions of waste concrete powder, 8-12 portions of slag, 0.5-0.8 portions of limestone, 0.15-0.2 portions of fiber, 2-5 portions of foaming agent, 1-2 portions of hydrophobic agent, 1-2 portions of water reducer and 80-120 portions of water. By screening concrete admixtures and compounding with appropriate mixing ratio and additives, the mechanical properties of filling materials, stability and durability after hardening are obviously improved.
【技术实现步骤摘要】
一种泡沫混凝土路桥填筑材料
本专利技术涉及建筑材料
，具体涉及一种泡沫混凝土路桥填筑材料。
技术介绍
目前，市政桥梁与路基结合处中常用的回填材料主要有砂砾土、级配砂、粘土等，由于此类材料自身重度大，强度较小，变形模量较小，而且在回填施工中填料的压实度往往难以达到规范要求，使得桥梁和路基结合处的差异沉降难以达到设计要求。泡沫轻质混凝土是一种轻质填筑材料，由水泥浆与一定比例的足够细小的稳定气泡群，经充分混合揽拌形成流体，并最终凝固成型。泡沫轻质混凝土质量轻、强度高且可调范围宽，拥有良好的自立性，且施工方便、快捷，具有较好的技术经济性。泡沫混凝土材料应用于路桥桥台背填充，具有强度大于常规回填土、填筑后形成一个整体、抗冲击性能好、无侧向压力、对地基荷载小等优势。使用泡沫混凝土填筑后，桥台背处于超固结状态，由此减少沉降和不均匀沉降、尽量减少台背路堤填料本身的工后沉降、避免桥头跳车病害，具有明显的技术优势。但是，现有的泡沫混凝土填筑材料其强度已经无法满足要求更高的道路桥梁，并且其稳定性较差，各方面性能随时间衰减较大，耐久性差。
技术实现思路
本专利技术的目的是提供一种泡沫混...
【技术保护点】
1.一种泡沫混凝土路桥填筑材料，其特征在于，包括：按重量份计，水泥100份、粉煤灰10‑15份、煤矸石陶粒5‑10份、废弃混凝土粉体20‑30份、矿渣8‑12份、石灰石0.5‑0.8份、纤维0.15‑0.2份、发泡剂2‑5份、憎水剂1‑2份、减水剂1‑2份以及水80‑120份。
【技术特征摘要】
1.一种泡沫混凝土路桥填筑材料，其特征在于，包括：按重量份计，水泥100份、粉煤灰10-15份、煤矸石陶粒5-10份、废弃混凝土粉体20-30份、矿渣8-12份、石灰石0.5-0.8份、纤维0.15-0.2份、发泡剂2-5份、憎水剂1-2份、减水剂1-2份以及水80-120份。2.根据权利要求1所述的泡沫混凝土路桥填筑材料，其特征在于，包括：按重量份计，水泥100份、粉煤灰12-14份、煤矸石陶粒6-8份、废弃混凝土粉体22-26份、矿渣8-10份、石灰石0.6-0.8份、纤维0.16-0.18份、发泡剂3-4份、憎水剂1.2-1.6份、减水剂1.5-1.8份以及水90-120份。3.根据权利要求1或2所述的泡沫混凝土路桥填筑材料，其特征在于，所述发泡剂为复合发泡剂，其包括：占复合发泡剂总质量70-80％的蛋白发泡剂、15-20％的稳泡剂以及5-10％的瞬凝剂。4.根据权利要求3所述的泡沫混凝土路桥填筑材料，其特征在于，所述复合发泡剂包括：占复合发泡剂总质量74-78％的蛋白发泡剂、16-18％的稳泡剂以及6-8％的瞬凝剂。5.根据权利要求3所述的泡沫混凝土路桥填筑材料，其特征在于，所述稳泡剂包括阿拉伯树胶、十二烷基苯磺酸钠、十二烷基硫酸钠和三乙醇胺，其质量比为1：(...
【专利技术属性】
技术研发人员：杨永红，王勇，邓安，张文瀚，
申请(专利权)人：中国五冶集团有限公司，中冶成都勘察研究总院有限公司，
类型：发明
国别省市：四川,51