The invention discloses a ceramic-like glass smooth wine bottle manufactured by a new process, which belongs to the field of glass products production. The raw materials used in the calculation of weight percentage include: broken glass 35%37%, quartz sand 25%27%, potassium feldspar 16%, albite 10%, sodium fluosilicate 7%, soda 4%, sodium hydroxide 1%; the process is as follows: crushed glass 35%37%, quartz sand 25%27%, potassium feldspar 16%, albite 10%, The finished product was prepared by mixing, melting, forming and annealing of raw materials. The glass-like smooth bottle of the product has beautiful appearance and is mainly used as the packaging of middle and high-grade liquor. The product has high density, pleasant knocking sound and good anti-falling effect.
【技术实现步骤摘要】
新工艺生产的仿陶玻璃光面酒瓶
本专利技术属于玻璃容器制造领域，尤其涉及一种新工艺生产的仿陶玻璃光面酒瓶。
技术介绍
玻璃的主要成分是二氧化硅，在熔融时形成连续网络结构，冷却过程中粘度逐渐增大并硬化而不结晶的硅酸盐类非金属材料，酒瓶的种类繁多，从原材料上来分，主要有晶面玻璃酒瓶（晶白料）和高白料玻璃酒瓶，晶白料玻璃的特点是二氧化硅含量较高，具有折射率高、晶莹剔透、密度较大的特点，当二氧化硅含量高了以后，熔制温度高、玻璃液粘度大，自动化生产有一定困难；而高白料酒瓶二氧化硅含量较低，但这种玻璃白度好、透明度高，原料要选择杂质少、纯度高的精料，必要时还需用酸液清洗原料，除去原料中的铁等杂质。随着科学技术的不断进步，玻璃酒瓶的品种越来越多，仿陶新工艺生产的玻璃光面酒瓶就是新产品的一种，仿陶指仿制陶器，陶器是指以粘土为胎，经过手捏、轮制、模塑等方法加工成型后，在800—1000℃高温下焙烧而成的器具，坯体不透明，有微孔，具有吸水性，叩之声音不清，陶器在古代作为一种生活用品，在现在一般作为工艺品收藏，陶器外表美观，生产的仿陶酒瓶并不是以生产陶器的方法来进行生产的真的陶器，而是在...
【技术保护点】
1.一种新工艺生产的仿陶玻璃光面酒瓶，生产该产品使用的原料按重量百分比计算包括：碎玻璃35%‑37%、石英砂25%‑27%、钾长石16%、钠长石10%、氟硅酸钠7%、纯碱4%、元明粉1%；其特征由以下步骤构成：（1）将配方量的碎玻璃、石英砂、钾长石、钠长石、氟硅酸钠、纯碱、元明粉送入掺混机掺混均匀得到混合料，用输送机将混合料送入电窑炉后开始升温，使混合料的温度达到1560℃‑1580℃并保持此温度31‑32小时，得到仿陶玻璃熔融体；（2）将定量的仿陶玻璃熔融体送入酒瓶模具，用吹制法吹制成所需酒瓶形状，此时仿陶玻璃酒瓶的温度降至1000℃‑1050℃时成型；（3）将成型的仿陶...
【技术特征摘要】
1.一种新工艺生产的仿陶玻璃光面酒瓶，生产该产品使用的原料按重量百分比计算包括：碎玻璃35%-37%、石英砂25%-27%、钾长石16%、钠长石10%、氟硅酸钠7%、纯碱4%、元明粉1%；其特征由以下步骤构成：（1）将配方量的碎玻璃、石英砂、钾长石、钠长石、氟硅酸钠、纯碱、元明粉送入掺混机掺混均匀得到混合料，用输送机将混合料送入电窑炉后开始升温，使混合料的温度达到1560℃-1580℃并保持此温度31-32小时，得到仿陶玻璃熔融体；（2）将定量的仿陶玻璃熔融体送入酒瓶模具，用吹制法吹制成所需酒瓶形状，此时仿陶玻璃酒瓶的温度降至...
【专利技术属性】
技术研发人员：孙鸿志，
申请(专利权)人：江苏新奥得玻璃制品股份有限公司，
类型：发明
国别省市：江苏,32