The invention discloses a sky-blue high aluminium glass. The glass masser percentage comprises the following components: 59-69 mol% SiO 2, 10-18 mol% Al2O3, 8-14 mol% Na2O, 1-3 mol% K2O, 2-8 mol% MgO, 0.1-0.4 mol% CaO, 0.01-0.03 mol% Selenium, 0.05-0.1 mol% Fe2O3 and 0.009-0.010 mol% CoO. On the basis of glass batch, sodium nitrate (0.9%) and C powder (0.02%) are added to obtain glass raw material after mixing evenly; glass liquid is obtained by heating and melting glass raw material; sky-blue high-alumina glass is obtained by casting and annealing glass liquid; while achieving the goal of sky-blue, the invention ensures the improvement of glass strength and hardness. The preparation process is simple and easy to realize.
【技术实现步骤摘要】
一种天蓝色高铝玻璃及其制备方法
本专利技术涉及有色玻璃制造
，具体是一种天蓝色高铝玻璃及其制备方法。
技术介绍
天蓝色的玻璃是装饰领域里的一种较受欢迎的颜色玻璃，传统的天蓝色玻璃基于钠钙硅玻璃体系，玻璃的强度与抗冲击性较差，受外力作用时易碎；此外,也有一些天蓝色玻璃是通过在普通普白或超白玻璃表面涂布或喷涂一层有机颜料的清漆或生漆来获得着色，但是该方法存在缺陷，因为涂层的质量和耐久性会随着时间而老化，同时热冲击还会导致涂层脱落，颜色自然也就随之变淡。而基于高强度、高硬度的高铝玻璃的海蓝色着色玻璃却未见有报道及其相关产品。
技术实现思路
本专利技术的目的在于提供一种天蓝色高铝玻璃及其制备方法，该玻璃具有高强度、高硬度的特性，且制备工艺简单，易于实现。本专利技术解决其技术问题所采用的技术方案是：一种天蓝色高铝玻璃，所述玻璃按摩尔百分比包含以下组分：59～69mol%的SiO2、10～18mol%的Al2O3、8～14mol%的Na2O、1～3mol%的K2O、2～8mol%MgO、0.1～0.4mol%的CaO、0.01～0.03mol%的硒、0.05～0.1mol%...
【技术保护点】
1.一种天蓝色高铝玻璃，其特征在于，所述玻璃按摩尔百分比包含以下组分：59～69 mol%的SiO2、10～18mol%的Al2O3、8～14 mol%的Na2O、1～3 mol%的K2O、2～8mol%MgO、0.1～0.4 mol%的CaO、0.01～0.03mol%的硒、0.05～0.1mol%的Fe2O3以及0.009～0.010mol%的CoO。
【技术特征摘要】
1.一种天蓝色高铝玻璃，其特征在于，所述玻璃按摩尔百分比包含以下组分：59～69mol%的SiO2、10～18mol%的Al2O3、8～14mol%的Na2O、1～3mol%的K2O、2～8mol%MgO、0.1～0.4mol%的CaO、0.01～0.03mol%的硒、0.05～0.1mol%的Fe2O3以及0.009～0.010...
【专利技术属性】
技术研发人员：彭寿，马立云，崔介东，操芳芳，曹欣，王巍巍，赵凤阳，仲召进，单传丽，石丽芬，倪嘉，韩娜，王萍萍，高强，
申请(专利权)人：中建材蚌埠玻璃工业设计研究院有限公司，
类型：发明
国别省市：安徽,34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。