The invention discloses a material composition for preparing a soft baby model, which comprises the following weight components: raw rubber 80 120 weight, fumed silica 22 35 weight, hydroxyl silicone oil 2 3 weight, vinyl triethoxysilane 12 15 weight, cellulose acetate 2 13 weight, metal hydroxide 0.1 0.5 weight, cyanoacrylic acid. Ester 5 26 by weight. The material composition of the invention belongs to a new type of macromolecule functional material, and the durability of the product is better when the baby model is prepared by using the material composition. After long-term use, the surface of the product will not yellowing and discoloration, and the durability of the material itself is better. The problem that the surface of the model prepared by using silica gel is easy to aging is solved.
【技术实现步骤摘要】
一种用于制备软质婴儿模型的材料组合物
本专利技术属于模型制备材料
，特别是涉及用于制备软质婴儿模型的材料组合物。
技术介绍
合格的专业护理人员必须经过多年的专业理论学习和临床实践，才能胜任本职工作。因为人的生命健康来不得半点失误，否则会造成严重的后果。所以护理人员在学习专业护理技能时，先要在人体模型上进行操作练习，由此产生仿真护理教学人体模型。人体模型是以人体参数为基础建立的，它可以用来准确描述人体形态特征和功能特征，是专业护理技能非常重要的一种辅助工具。医学模型所用材料目前主要为塑料材质，最终产品触感与真实人体相差较大，用户的使用感受较差。部分模型采用常规的硅胶材料进行制作，由于硅胶材质较软，用户使用时能够获得更加进行真实人体的触感，效果较好。但是，硅胶材料自身的耐久性较差，利用硅胶制备的模型存在表面易老化的问题。
技术实现思路
本专利技术的目的是提供一种用于制备软质婴儿模型的材料组合物，以解决利用硅胶制备的模型存在表面易老化，模型使用寿命短的问题。一种用于制备软质婴儿模型的材料组合物，包含以下组分：生胶、气相白炭黑、羟基硅油、乙烯基三乙氧基硅烷、醋酸丁酸纤维...
【技术保护点】
1.一种用于制备软质婴儿模型的材料组合物，其特征在于，包含以下组分：生胶、气相白炭黑、羟基硅油、乙烯基三乙氧基硅烷、醋酸丁酸纤维素、金属氢氧化物和氰基丙烯酸酯。
【技术特征摘要】
1.一种用于制备软质婴儿模型的材料组合物，其特征在于，包含以下组分：生胶、气相白炭黑、羟基硅油、乙烯基三乙氧基硅烷、醋酸丁酸纤维素、金属氢氧化物和氰基丙烯酸酯。2.根据权利要求1所述的用于制备软质婴儿模型的材料组合物，其特征在于，包含以下重量份的组分：生胶80-120重量份、气相白炭黑22-35重量份、羟基硅油2-3重量份、乙烯基三乙氧基硅烷12-15重量份、醋酸丁酸纤维素2-13重量份、金属氢氧化物0.1-0.5重量份、氰基丙烯酸酯5-26重量份。3.根据权利要求1所述的用于制备软质婴儿模型的材料组合物，其特征在于，包含以下重量份的组分：生胶100重量份、气相白炭黑28重量份、羟基硅油2.2重量份、乙烯基三乙氧基硅烷13重量份、醋酸丁酸纤维素9重量份、金属氢氧化物0.4重量份、氰基丙烯酸酯22重量份。4.根据权利要求1-3任一项所述的用于制备软质婴儿模型的材料组合物，其特征在于，所述生胶为乙烯基摩尔含量0.1％～0.15％的生胶。5....
【专利技术属性】
技术研发人员：徐文秀，
申请(专利权)人：北京高康科技发展有限公司，
类型：发明
国别省市：北京,11