The invention discloses a hollow plastic template, including synthetic resin, filler, plasticizer, stabilizer, additive and preservative. The proportion of each formula is 5%~6% of bamboo, 3%~4% of reed, 4%~5% of corn straw, 3%~5% of wheat straw, 45%~55% of synthetic resin, 15%~20% of filler, 15%~20% of plasticizer, 5%~8% of stabilizer, 1%~5% of additive and 3%~8% of preservative. The hollow plastic template prepared by the invention significantly improves the load-bearing performance of the plastic template, and the raw materials adopted by the invention include bamboo, reed, corn straw and wheat straw, which significantly reduces the production cost of the hollow plastic template.
【技术实现步骤摘要】
一种中空塑料模板的制备工艺
本专利技术涉及建筑模板
，具体涉及一种中空塑料模板的制备工艺。
技术介绍
塑料模板是在消化吸收欧洲先进的设备制造技术和半高的加工经验基础上坚持以先进的产品和工艺技术，通过高温200℃挤压而成的复合材料。塑料模板是一种节能型和绿色环保产品，是继木模板、组合钢模板、竹木胶合模板、全钢大模板之后又一新型换代产品。中空塑料模板是塑料模板的进一步发展，可以有效减轻塑料模板的重量，同时降低了生产成本，但是现有的中空塑料模板存在承重小，容易断裂的问题，同时现有的塑料模板采用的原材料成本较高。
技术实现思路
为了克服现有技术不足，本专利技术提供一种中空塑料模板的制备工艺，目的是提高中空塑料模板的承重，同时降低中空塑料建筑模板的生成成本。一种中空塑料模板，其特征在于：其配方包括合成树脂、填充料、增塑剂、稳定剂、添加剂和防腐剂，各配方的组成比例为竹子5%~6%、芦苇3%~4%、玉米秸秆4%~5%，小麦秸秆3%~5%、合成树脂45%~55%、填充料15%~20%、增塑剂15%~20%、稳定剂5%~8%、添加剂1%~5%和防腐剂3%~8%。优选的所述合成树脂...
【技术保护点】
1.一种中空塑料模板，其特征在于：其配方包括合成树脂、填充料、增塑剂、稳定剂、添加剂和防腐剂，各配方的组成比例为竹子5%~6%、芦苇3%~4%、玉米秸秆4%~5%，小麦秸秆3%~5%、合成树脂45%~55%、填充料15%~20%、增塑剂15%~20%、稳定剂5%~8%、添加剂1%~5%和防腐剂3%~8%。
【技术特征摘要】
1.一种中空塑料模板，其特征在于：其配方包括合成树脂、填充料、增塑剂、稳定剂、添加剂和防腐剂，各配方的组成比例为竹子5%~6%、芦苇3%~4%、玉米秸秆4%~5%，小麦秸秆3%~5%、合成树脂45%~55%、填充料15%~20%、增塑剂15%~20%、稳定剂5%~8%、添加剂1%~5%和防腐剂3%~8%。2.如权利要求1所述的一种中空塑料模板，其特征在于：所述合成树脂为聚乙烯。3.如权利要求1所述的一种中空塑料模板，其特征在于：所述填充料为玻璃纤维。4.如权利要求1所述的一种中空塑料模板，其特征在于：所述增塑剂为环氧硬脂酸辛脂。5.如权利要求1所述的一种中空塑料模板，其特征在于：所述稳定剂为环氧化物。6.如权利要...
【专利技术属性】
技术研发人员：赵成，钟秀娇，
申请(专利权)人：江苏正祥新材料有限公司，
类型：发明
国别省市：江苏,32