The invention relates to a covalent organic skeleton material with water discoloration and its preparation method and application. Firstly, covalent organic skeleton materials were synthesized by solid-state reaction at room temperature using p-phenylenediamine and Trimethylphenol as monomers. The covalent organic skeleton material of the present invention has large specific surface area and rich pore structure. By forming hydrogen bonds with water molecules, it can change its energy level, thereby changing its color, expanding the new application of covalent organic skeleton material in the field of catalysis, and the preparation method has the advantages of simple process, easy repetition, controllable structure and suitable for large-scale production.
【技术实现步骤摘要】
一种遇水变色共价有机骨架材料及其制备方法和应用
本专利技术属于多孔材料
，特别涉及一种遇水变色共价有机骨架材料的制备方法，并拓展共价有机骨架材料的潜在应用。
技术介绍
共价有机骨架材料是以C、N、O、B、Si等轻元素通过共价键结合形成的晶形多孔材料，由于COF具有高稳定性、结构规整性、孔隙可调性、易功能性，从而应用在气体储存、药物释放、催化和光电等领域。近期，共价有机骨架材料作为一种新型的多孔碳基材料由于其独特的性能如刚性结构(二维或三维)、较低的密度、高的稳定性以及较大比表面积和空隙等备受关注，这些特点使其有望解决非金属催化剂活性低、稳定性差等缺陷。共价有机骨架材料的常用合成方法有溶剂热法、离子热法、微波加热法等。CN103755588A公开了一种新型共价有机骨架光催化剂及其制备方法，该专利技术以均苯三甲醛和2,5-二(N,N-二甲基)氨基-1,4-苯二酰肼为合成单体采用溶剂热法制得共价有机骨架材料，该方法合成时间长、反应难调控、不利于大规模合成。
技术实现思路
为了克服现有技术中存在的不足，本专利技术利用静置法，在室温和开放体系下合成一种共价有机骨架材料。这...
【技术保护点】
1.一种遇水变色共价有机骨架材料，其特征在于，制备方法包括如下步骤：将有机溶剂和冰醋酸分散在蒸馏水中，形成混合溶液；将对苯二胺和三甲酰基苯酚分散在所形成的混合溶液中，室温下均匀搅拌0.1‑0.5h后，静置，过滤，所得固体粉末依次用四氢呋喃和丙酮洗涤后，于80℃真空干燥，得目标产物遇水变色共价有机骨架材料。
【技术特征摘要】
1.一种遇水变色共价有机骨架材料，其特征在于，制备方法包括如下步骤：将有机溶剂和冰醋酸分散在蒸馏水中，形成混合溶液；将对苯二胺和三甲酰基苯酚分散在所形成的混合溶液中，室温下均匀搅拌0.1-0.5h后，静置，过滤，所得固体粉末依次用四氢呋喃和丙酮洗涤后，于80℃真空干燥，得目标产物遇水变色共价有机骨架材料。2.根据权利要求1所述的一种遇水变色共价有机骨架材料，其特征在于：按摩尔比，对苯二胺:三甲酰基苯酚＝2:3。3.根据权利要求1所述的一种遇水变色共价有机骨架材料，其特征在于：所述的有机溶剂是四氢呋喃、1,3,5-三甲基苯、甲苯、二氧六环、乙醇、正丁醇和邻二氯苯的一种或二种以上的混合。4.根据权利要求3所述的一种遇水变色共价...