The invention provides a method for fast compacting and carbonizing to enhance wood properties, which includes the following steps: (1) drying wood; (2) placing wood on stainless steel electric heating board, placing a perforated metal plate on top of wood, heating and compressing wood to control the compression rate of wood at 6%25%, heat treatment at the pressure state for 1_30 min, cooling, pressure relief, and densification. Solid carbonization enhances wood. The processing method of the present invention realizes wood compaction and densification while carbonizing wood, and increases its density, thereby enhancing the surface hardness of wood and the bending strength of wood, that is, improving the mechanical properties of wood.
【技术实现步骤摘要】
一种快速密实炭化增强木材性能的处理方法
本专利技术属于木材处理领域，尤其涉及一种快速密实炭化增强木材性能的处理方法。
技术介绍
由于木材资源短缺，木材工业越来越依赖于速生材和幼龄材。然而，速生材和幼龄材存在许多天然缺陷：细胞壁中存在着较多的游离羟基和一些极性的官能团以及毛细管，使得不管是气态水还是液态水都能够轻而易举的进入木材，致使木材在加工使用过程中由于吸湿或者解吸作用而导致木材尺寸稳定性较差、由于水分侵入而导致耐久性差；同时，木材易产生破裂、翘曲变形现象，且易腐朽、易霉变。为此，木材加工业一直在寻找高效率、低成本、可持续以及效果好的木材加工处理方式，以降低木材或人造板水分的作用，从而来提高木材的尺寸稳定性，增强防霉防腐性、耐久性等，延长木材的使用寿命，拓宽木材的使用范围。炭化处理技术被认为是减少木材水分吸收的有效方法。炭化处理使木材的成分(如半纤维素和非晶态纤维素)优先降解，大大减少了木材中的羟基数量。由于半纤维素和非晶态纤维素是木材中含羟基数量最多的成分，羟基通过物理氢键结合吸附水分子。因此，炭化处理有效降低了木材的水分吸收，且处理材比未处理材的疏水性更好。...
【技术保护点】
1.一种快速密实炭化增强木材性能的处理方法，其特征在于，包括以下步骤：(1)将木材干燥；(2)将木材放到不锈钢电加热板上，用一块穿孔金属板置于木材上方，对木材进行加热加压压缩使木材的压缩率控制在6％‑25％，维持该压力状态热处理1‑30min，冷却，卸压，获得密实炭化增强木材。
【技术特征摘要】
1.一种快速密实炭化增强木材性能的处理方法，其特征在于，包括以下步骤：(1)将木材干燥；(2)将木材放到不锈钢电加热板上，用一块穿孔金属板置于木材上方，对木材进行加热加压压缩使木材的压缩率控制在6％-25％，维持该压力状态热处理1-30min，冷却，卸压，获得密实炭化增强木材。2.如权利要求1所述的制备方法，其特征在于，所述不锈钢电加热板进行加热的温度为150-350℃。3.如权利要求1所述的制备方法，其特征在于，所述不锈钢加热板加热至设定温度后再放置木材。4.如权利要求1所述的制备方法，其特征在于，所述不锈钢电加热板底部配有水冷却系统。5.如权...
【专利技术属性】
技术研发人员：杨守禄，姬宁，霍达，肖高寿，骆建林，罗梅，黄安香，赵毅，吴志刚，李丽芬，李丹，吴义强，张永权，李迅，丁建华，
申请(专利权)人：贵州省林业科学研究院，贵州六合门业有限公司，
类型：发明
国别省市：贵州,52