一种含锑铜基粉末冶金减摩材料制造技术

本发明专利技术公开了一种含锑铜基粉末冶金减摩材料，其包括以下重量份的组分：锡3‑5份、锌10‑12份、铅1‑3份、二硫化钼10‑12份、锑5‑10份、铜粉10‑20份、铈0.1‑0.3份、硫化铜5‑7份、混合稀土1‑5份、硅烷偶联剂5‑7份、硫化铁粉末5‑7份。硅烷偶联剂为异丁基三乙氧基硅、乙烯基三乙氧基硅烷、乙烯基三甲氧基硅烷中的一种或多种组合。本发明专利技术能够降低减摩材料的成本，同时本发明专利技术采用的配方稳定性更强，同时不会因为摩擦造成工件表面产生氧化层。

A Antimony-Containing Copper-Based Powder Metallurgy Friction Reducing Material

The invention discloses a antimony-containing copper-based powder metallurgical friction reducing material, which comprises the following components: tin 3 5, zinc 10 12, lead 1 3, molybdenum disulfide 10 12, antimony 5 10, copper powder 10 20, cerium 0.1 0.3, copper sulfide 5 7, mixed rare earth 1 5, silane coupling agent 5 7, iron sulfide powder 5. Silane coupling agent is one or more combinations of isobutyl triethoxysilane, vinyl triethoxysilane and vinyl trimethoxysilane. The invention can reduce the cost of friction reducing material, and the formula adopted by the invention has stronger stability, and does not cause oxide layer on the surface of the workpiece due to friction.

【技术实现步骤摘要】
一种含锑铜基粉末冶金减摩材料
本专利技术涉及一种冶金领域，具体是一种含锑铜基粉末冶金减摩材料。
技术介绍
粉末冶金减摩材料是用粉末冶金方法制造的﹑在相对运动中相互摩擦表面之间的摩擦系数较小的金属﹑合金或金属复合材料﹐又称烧结减摩材料。烧结减摩材料广泛用於制造滑动轴承﹑止推轴承﹑端面密封﹑支承衬套等。其主要优点是在有限润滑油的条件下﹐使用寿命较长和可靠性较高。烧结减摩材料按其制造方法可分为两类。一类是在材料孔隙中浸有润滑油或在材料成分中加有(或在其表层充覆)减摩剂或固体润滑剂(石墨﹑氧化物﹑硫化物﹑氮化物﹑氟塑料或其他塑料)。这类材料在干摩擦条件下依靠自身或表层含有的润滑剂润滑﹐即具有自润滑效果。另一类是钢与烧结合金的复合材料﹐如在钢带上烧结一层铜铅合金粉末等。这类材料的承载能力比前一类大﹐一般用以制造重载轴承。烧结减摩材料的发展趋向是提高多孔铁基和铜基材料的承载能力﹐发展能在较高温度和更恶劣的摩擦条件下使用的材料﹐研制能在真空和惰性气体中工作的材料。
技术实现思路
本专利技术的目的在于提供题目，以解决上述
技术介绍
中提出的问题。为实现上述目的，本说明提供如下技术方案：一种含锑铜基粉末冶金减本文档来自技高网...

【技术保护点】
1.一种含锑铜基粉末冶金减摩材料，其特征在于，其包括以下重量份的组分：锡3‑5份、锌10‑12份、铅1‑3份、二硫化钼10‑12份、锑5‑10份、铜粉10‑20份、铈0.1‑0.3份、硫化铜5‑7份、混合稀土1‑5份、硅烷偶联剂5‑7份、硫化铁粉末5‑7份。

【技术特征摘要】
1.一种含锑铜基粉末冶金减摩材料，其特征在于，其包括以下重量份的组分：锡3-5份、锌10-12份、铅1-3份、二硫化钼10-12份、锑5-10份、铜粉10-20份、铈0.1-0.3份、硫化铜5-7份、混合稀土1-5份、硅烷偶联剂5-7份、硫化铁粉末5-7份。2.根据权利要求1所述的一种含锑铜基粉末冶金减摩材料，其特征在于，其包括以下重量份的组分：锡3份、锌10份、铅1份、二硫化钼10份、锑5份、铜粉10份、铈0.1份、硫化铜5份、混合稀土1份、硅烷偶联剂5份...

【专利技术属性】
技术研发人员：汪杨志，
申请(专利权)人：汪杨志，
类型：发明
国别省市：湖北,42