The invention discloses a processing technology, which relates to the field of steel wire rope, in particular to a processing technology of plastic-coated steel wire rope. The processing technology of the plastic-coated steel wire rope includes the following steps: step 1: pretreatment; step 2: drawing; step 3: heat treatment; step 4: twisting strand into rope; step 5: plastic-coated treatment; the design of the invention is reasonable, and a plastic-coated steel rope is provided. The wire rope processing technology can avoid the oxidation and rust of the wire rope exposed to the air for a long time, and avoid the accidental scratch when people directly contact the body of the wire rope.
【技术实现步骤摘要】
包塑钢丝绳加工工艺
本专利技术涉及钢丝绳领域，尤其是涉及包塑钢丝绳加工工艺。
技术介绍
传统的钢丝绳直接暴露在空气中，容易发生氧化，于此同时，钢丝绳表面比较锋利，人们移动钢丝绳的时候容易发生意外割伤。
技术实现思路
本专利技术为解决上述提出到的问题，为此提供了一种包塑钢丝绳加工工艺，所述包塑钢丝绳加工工艺的步骤包括：步骤一；预处理：将不锈钢盘条置于放线架上，用机械进行清洁处理，清洁完成后进入涂硼设备进行涂硼处理，最后进入烘干设备烘干，得预处理线材；步骤二；拉拔：将预处理线材置于拉拔机进行多次拉拔，拉拔完成后收线得到半成品线材；步骤三；热处理：将拉拔处理后的半成品线材放入热处理炉进行加热处理，加热完成后进行清洗、冷却；步骤四；拧股成绳：将热处理后的半品线材放于拧股机上进行捻股合绳，得成品钢丝绳；步骤五；包塑处理：将钢丝绳放在塑料包覆机上进行包塑处理。作为优选，所述步骤三所述热处理炉的温度在700-800℃范围内。本专利技术的有益效果是：本专利技术设计合理，提供了一种包塑钢丝绳加工工艺，所述包塑钢丝绳加工工艺通过对钢丝绳进行包塑处理，避免钢丝绳长时间暴露在空气中氧化生锈，同时避免人们直接接触钢丝绳本体发生意外被划伤。具体实施方式本说明书中公开的所有特征，或公开的所有方法或过程中的步骤，除了互相排斥的特征和/或步骤以外，均可以以任何方式组合。本说明书的任一特征，除非特别叙述，均可被其他等效或具有类似目的的替代特征加以替换。即，除非特别叙述，每个特征只是一系列等效或类似特征中的一个例子而已。步骤一；预处理：将不锈钢盘条置于放线架上，用机械进行清洁处理，清洁完成后进入涂...
【技术保护点】
1.一种包塑钢丝绳加工工艺，其特征在于，所述包塑钢丝绳加工工艺将不锈钢作为原材料进行加工，它包括以下步骤：步骤一；预处理：将不锈钢盘条置于放线架上，用机械进行清洁处理，清洁完成后进入涂硼设备进行涂硼处理，最后进入烘干设备烘干，得预处理线材；步骤二；拉拔：将预处理线材置于拉拔机进行多次拉拔，拉拔完成后收线得到半成品线材；步骤三；热处理：将拉拔处理后的半成品线材放入热处理炉进行加热处理，加热完成后进行清洗、冷却；步骤四；拧股成绳：将热处理后的半品线材放于拧股机上进行捻股合绳，得成品钢丝绳；步骤五；包塑处理：将钢丝绳放在塑料包覆机上进行包塑处理。
【技术特征摘要】
1.一种包塑钢丝绳加工工艺，其特征在于，所述包塑钢丝绳加工工艺将不锈钢作为原材料进行加工，它包括以下步骤：步骤一；预处理：将不锈钢盘条置于放线架上，用机械进行清洁处理，清洁完成后进入涂硼设备进行涂硼处理，最后进入烘干设备烘干，得预处理线材；步骤二；拉拔：将预处理线材置于拉拔机进行多次拉拔，拉拔完成后收线得到半成品线材；步骤三；热...