The invention discloses a guitar neck coating and a preparation method thereof. Coatings include the following raw materials: acrylic resin, alkyd resin, n-butanol, epoxy resin, emulsified silicone oil, stearic amide and acrylate. The preparation method of guitar neck coating is to mix acrylic resin, alkyd resin, n-butanol and epoxy resin in the reactor. The reaction temperature is controlled at 30 50 C, stirring for 1 2 hours, then adding emulsified silicone oil, stearic amide and acrylate to the reactor. The temperature is controlled at 60 80 C, stirring for 1 2 hours, and finally grinding the mixture in the reactor. The slurry of 50 100 micron was obtained, that is, the guitar neck coating. The guitar neck processed with the paint prepared by the invention has the advantages of not easy to wrinkle, smooth, good scratch resistance and not easy to paint off.
【技术实现步骤摘要】
一种吉他琴颈涂料及其制备方法
本专利技术涉及吉他领域，特别是一种吉他琴颈涂料及其制备方法。
技术介绍
吉他，又译为结他或六弦琴。是一种弹拨乐器，通常有六条弦，形状与提琴相似。古典吉他与小提琴、钢琴并列为世界著名三大乐器。在弹奏吉他时，会有一只手扶住吉他琴颈进行按压琴弦，另一只手在吉他音孔处拨动琴弦，而变换和弦，按压琴弦的手部会顺着琴颈下上移动，这就需要吉他琴颈有一定的光滑度和抗刮性，而现有的吉他琴颈涂料制作的琴颈抗刮性不好，长期使用吉他，有时会出现掉漆的情况。
技术实现思路
本专利技术的目的在于，提供一种吉他琴颈涂料及其制备方法。用本专利技术制得的涂料加工的吉他琴颈，具有不易起皱、光滑，抗刮性好，不易掉漆的优点。本专利技术的技术方案：一种吉他琴颈涂料，按照重量份数计，涂料包括下列原料：丙烯酸树脂30-40份、醇酸树脂20-30份、正丁醇6-10份、环氧树脂10-20份、乳化硅油1-2份、硬脂酰胺1-2份和丙烯酸酯2-3份。前述的吉他琴颈涂料中，按照重量份数计，涂料包括下列原料：丙烯酸树脂32-38份、醇酸树脂22-28份、正丁醇7-9份、环氧树脂13-17份、乳化硅油...
【技术保护点】
1.一种吉他琴颈涂料，其特征在于：按照重量份数计，涂料包括下列原料：丙烯酸树脂30‑40份、醇酸树脂20‑30份、正丁醇6‑10份、环氧树脂10‑20份、乳化硅油1‑2份、硬脂酰胺1‑2份和丙烯酸酯2‑3份。
【技术特征摘要】
1.一种吉他琴颈涂料，其特征在于：按照重量份数计，涂料包括下列原料：丙烯酸树脂30-40份、醇酸树脂20-30份、正丁醇6-10份、环氧树脂10-20份、乳化硅油1-2份、硬脂酰胺1-2份和丙烯酸酯2-3份。2.根据权利要求1所述的吉他琴颈涂料，其特征在于：按照重量份数计，涂料包括下列原料：丙烯酸树脂32-38份、醇酸树脂22-28份、正丁醇7-9份、环氧树脂13-17份、乳化硅油1.2-1.8份、硬脂酰胺1.3-1.7份和丙烯酸酯2.4-2.6份。3.根据权利要求2所述的吉他琴颈涂料，其特征在于：按照...