The invention discloses the production process of antistatic flocking carpet, which includes the following steps: coating acrylic resin adhesive on carpet base material; flocking on the resin adhesive, the flocking process is a mixture of flocking PA66 fibers and conductive fibers, in which PA66 and conductive fibers are evenly mixed, and the content of conductive fibers is less than 5%; the carpet base material includes PVC layer and glass fibers. A cloth layer and a PVC layer, wherein the glass fiber cloth layer is a glass fiber cloth with steel wires. In flocking, the mixture of nylon fibers and conductive fibers is used to flock, in which the content of conductive fibers is less than 5%, so that the carpet has antistatic effect and meets the antistatic requirement of flocking carpet in high-speed railway application.
【技术实现步骤摘要】
抗静电植绒地毯生产工艺
本专利技术涉及植绒地毯,具体涉及一种抗静电植绒地毯生产工艺。
技术介绍
植绒就是指利用电荷同性相斥异性相吸的物理特性,使绒毛带上负电荷,把需要植绒的物体放在零电位或接地条件下,绒毛受到异电位被植物体的吸引,呈垂直状加速飞升到需要植绒的物体表面上,由于被植物体涂有胶粘剂,绒毛就被垂直粘在被植物体上。植绒地毯,因其使用场合的不同,对其性能需求不同,本专利技术针对高铁用植绒地毯的需求,设计了下述方案。
技术实现思路
针对高铁用植绒地毯需要具有抗静电性能的技术问题,本专利技术提供了一种抗静电植绒地毯生产工艺,在植绒时,通过利用尼龙纤维和导电纤维的混合物进行植绒,其中,导电纤维的含量不大于5%,从而使得地毯具有抗静电效果,满足植绒地毯在高铁应用的抗静电需求。为解决上述技术问题,本专利技术采用的一个技术方案是:抗静电植绒地毯生产工艺,包括以下工艺步骤,在地毯基材上涂覆丙烯酸树脂胶;在所述的树脂胶上进行植绒,该植绒过程为植PA66纤维和导电纤维的混合物,其中,PA66和导电纤维混合均匀,且导电纤维的含量不大于5%;所述的地毯基材包括PVC层、玻纤布层、PVC层,其中,所述的玻纤布层为夹钢丝玻纤布。在上述方案的基础上,作为优选,所述丙烯酸树脂胶中混有抗菌剂,且抗菌剂的添加量不大于丙烯酸树脂胶的5%。在上述方案的基础上,作为优选,所述PA66的长度为2mm,直径为1.5mm。在上述方案的基础上,作为优选,所述PA66的植绒密度为8600万根/平方米。本专利技术的有益效果是:在植绒时,通过利用尼龙纤维和导电纤维的混合物进行植绒,其中,导电纤维的含量不大于5 ...
【技术保护点】
1.抗静电植绒地毯生产工艺,其特征在于,包括以下工艺步骤,在地毯基材上涂覆丙烯酸树脂胶;在所述的树脂胶上进行植绒,该植绒过程为植PA66纤维和导电纤维的混合物,其中,PA66和导电纤维混合均匀,且导电纤维的含量不大于5%;所述的地毯基材包括PVC层、玻纤布层、PVC层,其中,所述的玻纤布层为夹钢丝玻纤布。
【技术特征摘要】
1.抗静电植绒地毯生产工艺,其特征在于,包括以下工艺步骤,在地毯基材上涂覆丙烯酸树脂胶;在所述的树脂胶上进行植绒,该植绒过程为植PA66纤维和导电纤维的混合物,其中,PA66和导电纤维混合均匀,且导电纤维的含量不大于5%;所述的地毯基材包括PVC层、玻纤布层、PVC层,其中,所述的玻纤布层为夹钢丝玻纤布。2.如权利要求1...