本发明专利技术涉及一种以废料为原料铸造铜合金的粉尘吸收剂的制备方法，包括以下步骤：（1）按比例称取十六烷基磺酸钠、二丁酸二辛酯磺酸钠、脂肪酸磺烷基酰胺、羧甲基淀粉、氧化锌、尿素、水余量；（2）将步骤（1）称取的原料稀释到质量百分比浓度为2‑4%后置于铸造炉四周。本发明专利技术制备的吸收剂具有制备简单，使用方便，吸收效率高等优点。

Preparation of a Dust Absorbent for Casting Copper Alloys Using Waste as Raw Material

The invention relates to a preparation method of dust absorbent for casting copper alloy with waste material, which includes the following steps: (1) proportionally weighing sodium hexadecyl sulfonate, sodium dioctyl butyrate sulfonate, fatty acid sulfonamide, carboxymethyl starch, zinc oxide, urea and water surplus; (2) diluting the weighted raw material to a mass percentage concentration of 2 4% and putting it back. Around the casting furnace. The absorbent prepared by the invention has the advantages of simple preparation, convenient use and high absorption efficiency.

【技术实现步骤摘要】
一种以废料为原料铸造铜合金的粉尘吸收剂的制备方法
：本专利技术属于化工
，涉及吸收剂的制备，具体涉及一种以废料为原料铸造铜合金的粉尘吸收剂的制备。
技术介绍
在铜合金铸造行业，尤其是非真空，以废旧料为原料铸造时，由于废料表面所吸附的油污、氧化物、夹杂物等，在加入炉中后在高温下很容易产生大量粉尘，需要迅速去除，传统的采用鼓风机等方式，但往往不能有效去除，并且还会造成更大面积的大气污染。
技术实现思路
：本专利技术的目的在于提供一种能够迅速吸附铜合金铸造过程中产生的粉尘且操作简单、成本低的吸收剂。本专利技术的技术方案如下：（1）按质量百分数称取下列各组分：十六烷基磺酸钠5～20％二丁酸二辛酯磺酸钠3～5％脂肪酸磺烷基酰胺6～8％羧甲基淀粉0.1～0.5％氧化锌0.1～0.5％尿素1～2％水余量；（2）将步骤（1）称取的原料稀释到质量百分比浓度为2-4%后置于铸造炉四周。进一步地，本专利技术原料组分的最优组成为：十六烷基磺酸钠18％二丁酸二辛酯磺酸钠3％脂肪酸磺烷基酰胺6％羧甲基淀粉0.3％氧化锌0.3％尿素1.5％水余量。与现有技术相比，本吸收剂是由表面活性剂复配而成，属于化学药品范畴本文档来自技高网...

【技术保护点】
1.一种以废料为原料铸造铜合金的粉尘吸收剂的制备方法，其特征在于，包括以下步骤：（1）按质量百分数称取下列各组分：十六烷基磺酸钠5～15％二丁酸二辛酯磺酸钠2～5％脂肪酸磺烷基酰胺4～8％羧甲基淀粉0.1～0.5％氧化锌0.1～0.5％尿素1～2％水余量；（2）将步骤（1）称取的原料稀释到质量百分比浓度为2‑4%后置于铸造炉四周。

【技术特征摘要】
1.一种以废料为原料铸造铜合金的粉尘吸收剂的制备方法，其特征在于，包括以下步骤：（1）按质量百分数称取下列各组分：十六烷基磺酸钠5～15％二丁酸二辛酯磺酸钠2～5％脂肪酸磺烷基酰胺4～8％羧甲基淀粉0.1～0.5％氧化锌0.1～0.5％尿素1～2％水余量；（2）将步骤（1）称取...