The invention provides a processing technology of water-soluble fibre and cashmere blended yarn, which is characterized by: water-soluble vinylon and cashmere are used as raw materials, in which water-soluble fibre accounts for 10%25% and cashmere 90%75%; water-soluble vinylon filament is mixed by water-soluble vinylon blending method, water-soluble vinylon filament is mixed by 7.7 tex filament, and water-soluble is added in the merging process; Sex vinylon staple fibers are blended into cashmere stripping and wool processing, and the products produced by the invention are fluffy, slippery, soft feel, unique style and lighter fabric structure, which have won market users and recognition.
【技术实现步骤摘要】
一种水溶性纤维与羊绒混纺纱的加工工艺
本专利技术属于纺织领域，尤其涉及一种水溶性纤维与羊绒混纺纱的加工工艺。
技术介绍
水溶性纤维易溶于水，纺纱加工过程，成品回潮过程，成品纱过程不同与正常的羊绒产品，通过对水溶性维纶长丝、短纤维、毛条与羊绒混纺产品的探讨，寻求混纺比范围、工艺流程、工艺参数及工艺过程控制、色纱生产对色控制、成品纱检验控制的方法。水溶性纤维是特色品种，分长丝和短纤两大类，在60～70℃完全溶于水，呈无色、无味、无毒、无色透明状水溶液，在短时间内能自然生物降解。维纶与羊绒纤维混纺，不仅丰富了精仿羊绒纱的品种，还弥补了羊绒纱的可纺支数，降低了精仿羊绒纱的纺纱难度。
技术实现思路
本专利技术的目的在于针对现有技术的不足而提供为实现上述目的，提供的产品蓬松、滑腻、柔软、独特的风格而更轻薄的织物。本专利技术的技术方案是：一种水溶性纤维与羊绒混纺纱的加工工艺，其特征在于：①采用原料为水溶性维纶和羊绒，其中水溶性纤维占比为10％-25％，羊绒占比为90％-75％；采用水溶性维纶混入方式，水溶性维纶长丝混入，采用的是线密度为7.7tex的长丝，在并线工序加入...
【技术保护点】
1.一种水溶性纤维与羊绒混纺纱的加工工艺，其特征在于：①采用原料为水溶性维纶和羊绒，其中水溶性纤维占比为10％‑25％，羊绒占比为90％‑75％；采用水溶性维纶混入方式，水溶性维纶长丝混入，采用的是线密度为7.7tex的长丝，在并线工序加入；水溶性维纶短纤维混入，在羊绒制条和毛工序加入；②工艺流程：水溶性维纶长丝混入为：精纺羊绒单纱(1根或2根)+1根水溶性维纶长丝‑倍捻‑回潮‑成品检验；③工艺控制：油剂选择及加油量控制，选用FX‑908和毛油，油水比1：6，抗静电剂Kataxal为油剂的2/3,加入量为原料投入量的25％以内，混合原料上机回潮率控制在25％左右；制条工艺中...
【技术特征摘要】
1.一种水溶性纤维与羊绒混纺纱的加工工艺，其特征在于：①采用原料为水溶性维纶和羊绒，其中水溶性纤维占比为10％-25％，羊绒占比为90％-75％；采用水溶性维纶混入方式，水溶性维纶长丝混入，采用的是线密度为7.7tex的长丝，在并线工序加入；水溶性维纶短纤维混入，在羊绒制条和毛工序加入；②工艺流程：水溶性维纶长丝混入为：精纺羊绒单纱(1根或2根)+1根水溶性维纶长丝-倍捻-回潮-成品检验；③工艺控制：油剂选择及加油量控制，选用FX-908和毛油，油水比1：6，抗静电剂Kataxal为油剂的2/3,加入量为原...