The invention discloses an aluminium plating stripping method for stainless steel surface, which comprises the following steps: S100, loosening aluminium plating on stainless steel liner surface by stripping solution; S200, removing aluminium plating on stainless steel liner surface after loosening by sandblasting, using a stripping solution composed of sodium hydroxide, sodium citrate, sodium carbonate and sodium lauryl sulfate, and the solvent is high purity water, and the stripping solution used is high purity water. The concentration of sodium hydroxide, sodium citrate, sodium carbonate, lauryl alcohol and sodium sulfate is 60-80g/L, 60-80g/L, 60-80g/L, and 3-5g/L respectively. Dry suction sand blasting machine is used for sand blasting, and the pressure of sand blasting is 4-6kg/cm.
【技术实现步骤摘要】
一种不锈钢表面铝镀层退镀方法
本专利技术涉及退镀液以及喷砂机领域，具体为一种不锈钢表面铝镀层退镀方法。
技术介绍
物理气相沉积(PhysicalVaporDeposition简称PVD)是用物理的方法(如蒸发、溅射等)使镀膜材料气化，在基体表面沉积成膜的方法。除传统的真空蒸发和溅射沉积技术外，还包括近30多年来蓬勃发展起来的各种离子束沉积，离子镀和离子束辅助沉积技术。其沉积类型包括:真空蒸镀、溅射镀、离子镀等。物理气相沉积技术虽然五花八门，但都必须实现气相沉积三个环节，即镀料(靶材)气化一气相输运一沉积成膜。物理气相沉积(PVD)中的磁控溅射技术具有设备简单、易于控制、镀膜面积大和膜层附着力强的很多优点，生产过程无污染，是一种绿色环保的表面防护技术，发展前景广阔。但是，利用磁控溅射方法镀膜时，镀膜机内部不锈钢衬板也会被镀上膜层。为了保证镀膜机的使用效果，需要对不锈钢衬板进行退镀，现有的用于不锈钢衬板的退镀方法通常是采用喷砂，通过喷砂处理能够去除不锈钢衬板上的镀层。但是，喷砂退镀的铝层厚度不能超过300μm，铝镀层厚度过大时，喷砂无法达到退镀效果，这样使得不锈钢衬板...
【技术保护点】
1.一种不锈钢表面铝镀层退镀方法，其特征在于：包括如下步骤：S100、通过退镀液疏松不锈钢衬板表面的铝镀层；S200、通过喷砂去除不锈钢衬板表面疏松后的铝镀层。
【技术特征摘要】
1.一种不锈钢表面铝镀层退镀方法，其特征在于：包括如下步骤：S100、通过退镀液疏松不锈钢衬板表面的铝镀层；S200、通过喷砂去除不锈钢衬板表面疏松后的铝镀层。2.根据权利要求1所述的一种不锈钢表面铝镀层退镀方法，其特征在于：在步骤S100中，所用的退镀液的成分为：氢氧化钠；柠檬酸钠；碳酸钠；月桂醇硫酸钠；溶剂为高纯水。3.根据权利要求1所述的一种不锈钢表面铝镀层退镀方法，其特征在于：在步骤S100中，所用的退镀液中：氢氧化钠的浓度为60～80g/L；柠檬酸钠的浓度为3～5g/L；碳酸钠的浓度为60～80g/L；月桂醇硫酸钠的浓度为3～5g/L。4.根据权利要求1所述的一种不锈钢表面铝镀层退镀方法，其特征在于：在步骤S100中，制备退镀液的具体步骤为：S101、根据使用需求将所需质量的高纯水加入反应容器中，并依次向反应容器中按照浓度配比加入氢氧化钠、柠檬酸钠和月桂醇硫酸钠，搅拌均匀直至溶质完全溶...
【专利技术属性】
技术研发人员：夏原，李阳，张延杰，
申请(专利权)人：包头中科泰磁涂层科技有限责任公司，
类型：发明
国别省市：内蒙古,15