The invention relates to a lead sulfide film, which belongs to the preparation field of semiconductor materials. The method adopts lead acetate and sulfur powder, which are lead source and sulfur source respectively. Sodium thiosulfate is prepared by using sulfur powder and sodium sulfite as raw materials, potassium sodium tartrate as complexing agent, pH value is adjusted by potassium hydroxide, and the deposited liquid is placed in a water bath pot, heated at 75 ~C for 4 hours, and then dried to obtain lead sulfide film. The method has the advantages of easy availability of raw materials, simple process, low cost, high yield and large-scale production of thin films, so the method has very broad application prospects.
【技术实现步骤摘要】
一种硫化铅薄膜
本专利技术涉及一种硫化铅薄膜，该方法简便易行，无毒环保，具有普适性，能够在实验室中进行快速有效的制备，属于半导体材料的制备领域。
技术介绍
硫化铅薄膜是一类重要的半导体材料，窄禁带(0.41eV)较并且激发玻尔半径（18nm）较大，因为其介电常数较大，折射率高，可以制成具有高折射率的红外光学薄膜，并且广泛的应用于制造红外探测器、激光发射器、热电转换器、太阳能电池、发光二极管、超离子材料、薄膜晶体管等半导体器件。该材料在国防及工、农业建设中得到了大规模应用，近几十年来受到了科学界的广泛重视。制备硫化铅薄膜的方法有很多，如低温水热法、化学反应法（CRM）、电化学沉积法（ECD）、连续离子反应法、溶胶-凝胶法（SGM）等。与这些制备方法比较，化学液相法从性能价格比上来说具有明显的优势，是广泛应用的一种方法。在相对较低的温度下，不需要任何特殊的设置和任何复杂的仪器，且制备的薄膜晶粒更加紧密，表面更加光滑。化学液相法具有成本低、收率高和能大规模生产薄膜等特点，在合成金属硫族化物晶体时有很大前景。对比论文文献：刘峰.化学液相法制备PbS红外光电薄膜及其性能研究...
【技术保护点】
1.一种硫化铅薄膜，主要特征在于：包括0.2mol/L醋酸铅、1 mol/L酒石酸钾钠、5g硫粉、12g亚硫酸钠、氢氧化钾，制备过程如下：制备前对衬底进行去油、去污清洗，放入无水乙醇中经过超声波清洗后，再放入无水乙醇中浸泡，沉积时使用；配制出0.2mol/L的醋酸铅溶液，1mol/L的酒石酸钾钠溶液和0.2mol/L硫代硫酸钠溶液；边搅拌边将30mL的醋酸铅溶液、20mL的酒石酸钾钠溶液和6～8mL硫代硫酸钠溶液混合，再使用氢氧化钾溶液调节pH值至11.0～12.0，加入去离子水至100mL；吹干后放入75℃的沉积液中，4小时后取出衬底。
【技术特征摘要】
1.一种硫化铅薄膜，主要特征在于：包括0.2mol/L醋酸铅、1mol/L酒石酸钾钠、5g硫粉、12g亚硫酸钠、氢氧化钾，制备过程如下：制备前对衬底进行去油、去污清洗，放入无水乙醇中经过超声波清洗后，再放入无水乙醇中浸泡，沉积时使用；配制出0.2mol/L的醋酸铅溶液，...
【专利技术属性】
技术研发人员：孙喜桂，石磊，张艺宁，张云瑞，王建鹏，汪嘉一，
申请(专利权)人：山东建筑大学，
类型：发明
国别省市：山东,37