本发明专利技术公开了一种提高磷酸二铵的表面玻璃感的方法，包括以下步骤：在磷酸生产磷酸二铵的常规方法中，其特征在于：在中和槽中添加一种占中和槽磷酸质量的0.05～0.20％的硼酸，硼酸为弱酸。本发明专利技术方法主要改善磷酸二铵粒子的透感、光泽、强度等性能，同时能够使磷酸二铵中含硼微量元素，对许多作物有肥效，能增进作物品质和提高产量。而且还具有杀虫和催化剂效果。

A Method for Improving Surface Glass Sensitivity of Diammonium Phosphate

The invention discloses a method for improving the surface glass sensitivity of diammonium phosphate, which includes the following steps: in the conventional method of producing diammonium phosphate with phosphoric acid, the characteristics are: adding a boric acid which accounts for 0.05-0.20% of the phosphoric acid quality of the neutralization tank, and the boric acid is weak acid. The method of the invention mainly improves the permeability, luster, strength and other properties of diammonium phosphate particles, at the same time can make the boron-containing trace elements in diammonium phosphate, has fertilizer effect on many crops, can improve crop quality and improve yield. It also has insecticidal and catalytic effects.

【技术实现步骤摘要】
一种提高磷酸二铵的表面玻璃感的方法
本专利技术涉及磷酸二铵的生产领域，具体来说，涉及磷酸二铵造粒的生产领域。
技术介绍
随着市场不断发展，用户对磷酸二铵产品的质量要求也不断提升。特别是对磷酸二铵的外观质量要求很高，对于控制好产品粒度、圆润度、色度、结晶感将成为磷酸二铵产品质量的直观标准。提升DAP产品外观质量是树立产品形象和用户质感的重要手段之一，在保证内在质量的前提下，通常DAP产品粒子外观质量由以下几项指标进行检验、判定:1、粒度:用孔径为1.00－4.00mm的试验筛筛分样品计算其所占的分率；而粒子大小规格趋于一致的程度，称为粒子均匀度。目前磷酸二铵粒度在90-92％2圆整度:颗粒外表轮廓圆弧呈球形的程度。少数企业用筛分法先将样品粒度为2.5－3.5mm的粒子分级出来，然后从中随机取数十颗粒子，以其在表面光滑的斜板上自由滚落到预设基准距离的数量占抽样数的分率(通常情况下，较圆的粒子自由滚落的距离相对远一些)作为衡量标准，其数值一一般在60％－80％，数值越大，说明粒子越圆。而圆润度则是颗粒在光线下肉眼直观感觉其球形和油润性的程度。3、颗粒强度:使用颗粒强度仪测量粒子的破碎压力，本文档来自技高网...

【技术保护点】
1.一种提高磷酸二铵的表面玻璃感的方法，包括以下步骤：在磷酸生产磷酸二铵的常规方法中，其特征在于：在中和槽中添加一种占中和槽磷酸质量的0.05～0.20％的硼酸。

【技术特征摘要】
1.一种提高磷酸二铵的表面玻璃感的方法，包括以下步骤：在磷酸生产磷酸二铵的常规方...