The invention discloses a simple synthesis method of spin-valve magnetoresistive composite CoFe2O4 Fe3O4. Using nano-magnetic iron oxide gamma Fe2O3 and CoO as raw materials, dried nano-magnetic iron oxide gamma Fe2O3 is added to alcohol for ball milling, then dried CoO is mixed with nano-magnetic iron oxide gamma Fe2O3, ball milling, pressing, and sintering in argon atmosphere, and finally forming in furnace. A series of spin-valve magnetoresistance composites CoFe2O4_Fe3O4 were prepared by cooling to room temperature. The device and the preparation process of the invention are simple, high repeatability and excellent magnetoresistance performance of the spin valve type.
【技术实现步骤摘要】
一种自旋阀型磁阻复合材料CoFe2O4-Fe3O4的简易合成方法
本专利技术属于磁阻复合材料的合成
，具体涉及一种自旋阀型磁阻复合材料CoFe2O4-Fe3O4的简易合成方法。
技术介绍
磁电阻(MR)效应是指导体或半导体在磁场作用下其电阻值发生变化的现象。Thomson于1857年发现了铁磁晶体的各向异性磁电阻效应(AnisotropicMagnetoresistance，AMR；ThomsonW.EffectsofmagnetizationontheelectricconductivityofNickelandofIron.Proc.Roy.Soc.1857,8:546-550)。1988年法国巴黎大学Fert研究小组M.N.Baibich等人开展了有关Fe/Cr超晶格的物性研究，该研究最终导致了GMR效应的发现(BaibichMN,BrotoJM,FertA,etal.Giantmagnetoresistanceof(001)Fe/(001)Crmagneticsuperlattices.Phys.Rev.Lett.1988,61:2472-2475)...
【技术保护点】
1.一种自旋阀型磁阻复合材料CoFe2O4‑Fe3O4的简易合成方法，其特征在于具体步骤为：步骤S1：将经过干燥处理的纯度为99.5%的纳米磁性氧化铁γ‑Fe2O3粉末加入酒精后球磨处理10‑24h得到泥状物；步骤S2：将步骤S1得到的泥状物进行干燥处理后用玛瑙研钵研磨均匀得到处理后的纳米磁性氧化铁γ‑Fe2O3粉末；步骤S3：将纯度为99%的CoO粉末干燥处理后与步骤S2得到的处理后的纳米磁性氧化铁γ‑Fe2O3粉末混合，再将混合后的粉末加入酒精后置于球磨罐内球磨处理10‑24h使粉末混合均匀，然后干燥处理得到混合粉末；步骤S4：将步骤S3得到的混合粉末用4MPa的压力压...
【技术特征摘要】
1.一种自旋阀型磁阻复合材料CoFe2O4-Fe3O4的简易合成方法，其特征在于具体步骤为：步骤S1：将经过干燥处理的纯度为99.5%的纳米磁性氧化铁γ-Fe2O3粉末加入酒精后球磨处理10-24h得到泥状物；步骤S2：将步骤S1得到的泥状物进行干燥处理后用玛瑙研钵研磨均匀得到处理后的纳米磁性氧化铁γ-Fe2O3粉末；步骤S3：将纯度为99%的CoO粉末干燥处理后与步骤S2得到的处理后的纳米磁性氧化铁γ-Fe2O3粉末混合，再将混合后的粉末加入酒精后置于球磨罐内球磨处理10-24h使粉末混合均匀，然后干燥处理得到混合粉末；步骤S4：...
【专利技术属性】
技术研发人员：王金凤，庄照通，节闯，
申请(专利权)人：河南师范大学，
类型：发明
国别省市：河南,41