The invention discloses an external wall thermal insulation material and a preparation method thereof. According to the weight of raw materials, the exterior wall insulation materials include 45 55 Portland cement, 3.5 4.5 portions aramid fiber, 20 30 portions flame retardant, 30 75 portions water glass, 10 20 portions vitrified beads, 0.8 1.2 portions water repellent, 5 11 portions gypsum powder, 15 25 portions fly ash, 5 10 portions aluminium silicate fiber asbestos. The exterior wall insulation material provided by the invention combines Portland cement, aramid fiber, vitrified beads, water repellent, etc. It has not only high strength, light weight, heat insulation, high weather resistance, waterproof and ultraviolet resistance, but also excellent fire and heat insulation performance, and is suitable for wide application.
【技术实现步骤摘要】
一种外墙保温材料及其制备方法
本专利技术涉及建筑材料领域，具体涉及一种外墙保温材料及其制备方法。
技术介绍
当今，全球保温隔热材料正朝着高效、节能、薄层、隔热、防水外护一体化方向发展，在发展新型保温隔热材料及符合结构保温节能技术的同时，更强调有针对性地使用保温隔热材料，按标准规范设计及使用，努力提高保温效率；这类材料在国内外已经广泛应用到建筑和工业设施中。其中，建筑物的隔热保温是节约能源、改善居住环境和使用功能的一个重要方面。建筑能耗在人类整个能源消耗中所占比例一般在30％-40％，因此建筑节能意义重大，在建筑和工业中采用良好的保温技术与材料，往往能起到事半功倍的效果。
技术实现思路
本专利技术提供一种外墙保温材料，能够具有保温、隔热、防火的效果。本专利技术一方面提供一种外墙保温材料，按原料重量份计，包括：硅酸盐水泥45-55份、芳纶纤维3.5-4.5份、阻燃剂20-30份、水玻璃30-75份、玻化微珠10-20份、憎水剂0.8-1.2份、石膏粉5-11份、粉煤灰15-25份、硅酸铝纤维棉5-10份。所述的外墙保温材料，优选的，所述憎水剂为硅烷基粉末憎水剂。所述的外墙...
【技术保护点】
1.一种外墙保温材料，其特征在于，按原料重量份计，包括：硅酸盐水泥45‑55份、芳纶纤维3.5‑4.5份、阻燃剂20‑30份、水玻璃30‑75份、玻化微珠10‑20份、憎水剂0.8‑1.2份、石膏粉5‑11份、粉煤灰15‑25份、硅酸铝纤维棉5‑10份。
【技术特征摘要】
1.一种外墙保温材料，其特征在于，按原料重量份计，包括：硅酸盐水泥45-55份、芳纶纤维3.5-4.5份、阻燃剂20-30份、水玻璃30-75份、玻化微珠10-20份、憎水剂0.8-1.2份、石膏粉5-11份、粉煤灰15-25份、硅酸铝纤维棉5-10份。2.根据权利要求1所述的外墙保温材料，其特征在于，所述憎水剂为硅烷基粉末憎水剂。3.根据权利要求2所述的外墙保温材料，其特征在于，所述阻燃剂采用三氧化二锑阻燃剂。4.根据权利要求3所述的外墙保温材料，其特征在于，所述芳纶纤维的长度为1.5-2.5毫米。5.根据权利要求4所述的外墙保温材料，其特征在于，按原料重量份计，包括：硅酸盐水泥50份、芳纶纤维4份、三氧化二锑阻燃剂25份、水玻璃55份、玻化微珠15份，硅烷基粉末憎水剂1份、石膏粉8份、粉煤灰20份、硅酸铝纤维棉8份；其中，所述芳纶纤维的长度为2毫米。6.一种外墙保温材料的制备方法，其特征在于，包括：按原料重量份计，将硅酸盐水泥45-55份、芳纶纤维3.5-4.5份、阻燃剂20-30份、水玻璃30...