The invention provides a high weatherproof true stone paint. The composition is made of the following raw materials: 35 to 45 parts of artificial color fine sand, the fineness of which is 80 meshes to 120 meshes; 15 to 25 parts of artificial color medium sand, the fineness of which is 40 meshes to 80 meshes; 5 to 10 parts of artificial coarse sand, the fineness of which is 10 meshes to 20 meshes; and 100 to 150 parts of organic sand. Silicone modified acrylate emulsion; 5 (10) carboxymethyl cellulose (CMC); 70 100 100 aggregates; 0.05 0.25 0.25 defoamer, 5~10 film builder. The formula optimizes the proportion of artificial color fine sand, middle sand and coarse sand, and optimizes the type and amount of the emulsion, and selects the glass bead as the aggregate to improve the weatherability of the real stone paint.
【技术实现步骤摘要】
一种高耐候真石漆
本专利技术属于涂料领域，尤其是涉及一种高耐候真石漆。
技术介绍
真石漆主要由高分子聚合物、彩石砂及相关助剂制成，干结固化后坚硬如石，与天然真石的效果高度一致，且具有硬度高，防火、耐酸碱、耐污染等特点，因此广泛应用于各种外墙装饰施工。现有技术中，采用将各种颜色、颗粒级配的天然彩砂，以乳液为基料，并辅以各种助剂制得的高仿真天然石材涂料，往往存在色差较大、且经过自然风化后其色差更为明显，且耐候性能较差，因此提供一种改进的高耐候真石漆成为现有技术中亟待解决的问题。
技术实现思路
为解决前述技术问题，本专利技术提供了一种高耐候真石漆，其特征是所述组合物由以下重量份数的原料制成：35-45份的人工彩细砂，所述人工彩细砂的细度为80目-120目；15-25份的人工彩中砂，所述人工彩中砂的细度为40目-80目5-10份的人工粗沙，所述的粗沙的细度为10目-20目；100-150份的有机硅改性丙烯酸酯乳液；5-10份的羧甲基纤维素(CMC)；70-100份的骨料；0.05-0.25重量份的消泡剂，5～10份的成膜助剂。所述的一种高耐候真石漆，其特征是所述骨料为玻璃微珠...
【技术保护点】
1.一种高耐候真石漆，其特征是所述真石漆由以下重量份数的原料制成：35‑45份的人工彩细砂，所述人工彩细砂的细度为80目‑120目；15‑25份的人工彩中砂，所述人工彩中砂的细度为40目‑80目5‑10份的人工粗沙，所述的粗沙的细度为10目‑20目；100‑150份的有机硅改性丙烯酸酯乳液；5‑10份的羧甲基纤维素(CMC)；70‑100份的骨料；0.05‑0.25重量份的消泡剂，5～10份的成膜助剂。
【技术特征摘要】
1.一种高耐候真石漆，其特征是所述真石漆由以下重量份数的原料制成：35-45份的人工彩细砂，所述人工彩细砂的细度为80目-120目；15-25份的人工彩中砂，所述人工彩中砂的细度为40目-80目5-10份的人工粗沙，所述的粗沙的细度为10目-20目；100-150份的有机硅改性丙烯酸酯乳液；5-10份的羧甲基纤维素(CMC)；70-100份的骨料；0.05-0.25重量份的消泡剂，5～10份的成膜助剂。2.如权利要求1所述的一种高...