A method for synthesizing high silica-aluminium ratio mordenite from microporous aluminium phosphite NKX 12 as aluminium source is described. The method is characterized by using a microporous aluminium phosphite NKX 12 containing structural terminal hydroxyl (Al OH) as aluminium source, using thin layer chromatography silica gel, silica sol or precipitation silica as silica source, and forming a mixture according to the molar ratio of Na2O:Al2O3:SiO 2:H=4-6:1-1.2:30:250-324. In the medium, the gel was stirred evenly, then transferred to the stainless steel kettle, and then crystallized for 1~5 days at 170~190 degree and autogenous pressure. The product was then cooled, washed and dried by conventional molecular sieve post-treatment.
【技术实现步骤摘要】
一种用微孔亚磷酸铝NKX-12为铝源合成高硅铝比丝光沸石的方法
本专利技术涉及一种不使用有机模板剂合成高硅铝比丝光沸石的方法，具体讲就是以一种含有结构端羟基(Al-OH)的微孔亚磷酸铝NKX-12为铝源，薄层层析硅胶、或硅溶胶、或沉淀法白炭黑为硅源，不添加有机模板剂制备高硅铝比丝光沸石。技术背景丝光沸石结构独特，共边相连的五元环对之间通过四元环联接成链，链之间以八元环联接形成直筒型十二元环主孔道，特殊的结构使得丝光沸石可能成为直链烷烃异构化催化剂。然而，常规丝光沸石组成为Na8(H2O)24[Al8Si40O96]，硅铝比(SiO2/Al2O3的摩尔比)仅为10，使丝光沸石作为烷烃异构化催化剂的酸性较弱，需要比较高的反应温度，而且反应过程中极易因水蒸汽作用脱铝使结构完整性破坏，影响催化性能，如C5/C6烷烃异构化反应就需要高硅铝比的(SiO2/Al2O3≥20)丝光沸石。合成高硅铝比(SiO2/Al2O3≥20)丝光沸石通常需要使用有机模板剂，但是，这样会使制备的丝光沸石产品成本增加，并在制备、产品后处理过程中产生污染，因此，不使用有机模板剂合成高硅铝比丝光沸...
【技术保护点】
1.一种用微孔亚磷酸铝NKX‑12为铝源合成高硅铝比丝光沸石的方法，其特点在于使用一种含有结构铝‑氧端羟基(Al‑OH)的微孔亚磷酸铝NKX‑12为铝源，将其与硅源、无机碱氢氧化钠和水按照摩尔比Na2O∶Al2O3∶SiO2∶H2O＝4～6∶1～1.2∶30∶250～324形成混合物，搅拌30～60分钟，形成均匀的混合物，然后转移至不锈钢釜中，于170～190℃和自生压力下水热晶化1～5天，按常规的分子筛后处理方法，冷却，洗涤，干燥，收集产品。
【技术特征摘要】
1.一种用微孔亚磷酸铝NKX-12为铝源合成高硅铝比丝光沸石的方法，其特点在于使用一种含有结构铝-氧端羟基(Al-OH)的微孔亚磷酸铝NKX-12为铝源，将其与硅源、无机碱氢氧化钠和水按照摩尔比Na2O∶Al2O3∶SiO2∶H2O＝4～6∶1～1.2∶30∶250～324形成混合物，搅拌30～60分钟，形成均匀的混合物，然后转移至不锈钢釜中，于170～190℃和自生压力下水热晶化1～5天，按常规的分子筛后处理方法，冷却，洗涤，干燥，收集产品。2.按照权利要求1所述的一种用微孔亚磷酸铝NKX-12为铝源合成高硅...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。