一种超低静电包装基膜及其生产方法技术

本发明专利技术公开了一种超低静电包装基膜，由以下质量比的原料组成：聚丙烯97.5‑99.2％；乙氧基化烷基胺0.4‑1.25％；乙氧基月桂酸胺0.4‑1.25％。乙氧基化烷基胺是很有效的抗静电剂，即使是在相对湿度低的情况下亦然，而且长期有效，乙氧基月桂酸胺适用于在湿度小的环境里使用，试验中发现有速效长效的抗静电功能，通过乙氧基化烷基胺和乙氧基月桂酸胺复配使用达到速效、长效、高效的目的，克服了通用抗静电剂迁移受温度影响、受时间影响。

A Ultra-Low Electrostatic Packaging Base Film and Its Production Method

The invention discloses an ultra-low electrostatic packaging base film, which consists of raw materials with the following mass ratio: polypropylene 97.5 99.2%; ethoxylated alkylamine 0.4 1.25%; ethoxylauric acid amine 0.4 1.25%. Ethoxylated alkylamine is a very effective antistatic agent, even in the case of low relative humidity. It is also effective for a long time. Ethoxylauric amine is suitable for use in low humidity environment. It has been found that the quick-acting and long-acting antistatic function can be achieved by the combination of ethoxylated alkylamine and ethoxylauric amine, which overcomes the shortcoming of quick-acting, long-acting and high-efficiency. The migration of general antistatic agents is affected by temperature and time.

【技术实现步骤摘要】
一种超低静电包装基膜及其生产方法
本专利技术涉及包装基膜材料
，具体讲是一种超低静电包装基膜及其生产方法。
技术介绍
市场的BOPP薄膜表面电阻通常在10的12-13次方，这样膜由于运行所带静电不能传导出去。薄膜在印刷中会生产印刷不良现象、存放使用中会吸附灰尘影响产品外观，这就需要使用抗静电剂。抗静电剂有阴离子型抗静电剂、阳离子型抗静电剂，考虑实际使用中有热稳定性差等因素，在BOPP中多为非离子型抗静电剂，常见胺类或酯类抗静电剂。考虑抗静电剂的要求达到其效果，需有效的迁移到膜的表面，考虑所选型抗静电剂与PP相容性问题是选型必须平衡的，常用抗静电剂不能很好的迁移到膜的表面。抗静电剂使用太多会影响膜的表观质量，太低则会达不到实际要求的低静电效果。所以，如何研制出一种抗静电效果好且基本质量好的包装基膜即为本领域工作人员所欲研究的方向。
技术实现思路
鉴于上述现有技术的缺陷，本专利技术的一个目的在于：提供一种超低静电包装基膜及其生产方法。为解决上述问题，本专利技术的技术解决方案是：一种超低静电包装基膜，由以下质量比的原料组成：聚丙烯97.5-99.2％；乙氧基化烷基胺0.4-1.25％；乙本文档来自技高网...

【技术保护点】
1.一种超低静电包装基膜，其特征在于由以下质量比的原料组成：聚丙烯 97.5‑99.2％；乙氧基化烷基胺 0.4‑1.25％；乙氧基月桂酸胺 0.4‑1.25％。

【技术特征摘要】
1.一种超低静电包装基膜，其特征在于由以下质量比的原料组成：聚丙烯97.5-99.2％；乙氧基化烷基胺0.4-1.25％；乙氧基月桂酸胺0.4-1.25％。2.一种超低静电包装基膜的生产方法，其特征在于包括以下步骤：(1)将聚丙烯、乙氧基化烷基胺以1:1的比例复配制成母料，然后将母料加入到聚丙烯中进行...