一种三元乙丙橡胶泡沫材料及其制备方法和用途技术

本发明专利技术提供一种三元乙丙橡胶泡沫材料的制备方法，所述的制备方法包括以下步骤：将造孔材料与三元乙丙橡胶基体复合，采用HF溶液腐蚀剔除造孔材料即形成所述三元乙丙橡胶泡沫材料。采用本申请中技术方案具有成本低廉，性能可调，生产过程简单的优点，同时，形成的三元乙丙橡胶泡沫材料具有低密度、高强度和高能量吸收性能，在汽车保险杠领域具有应用价值。

Three component ethylene propylene rubber foam material and preparation method and use thereof

The invention provides a preparation method of three element ethylene propylene rubber foam material. The preparation method comprises the following steps: compounding the pore forming material and the three element ethylene propylene rubber matrix, and adopting HF solution to corrode and eliminate the pore forming material, namely forming the three yuan ethylene propylene rubber foam material. The technical proposal of this application has the advantages of low cost, adjustable performance and simple production process. At the same time, the three component ethylene propylene rubber foam material has low density, high strength and high energy absorption performance, and has application value in the field of automobile bumper.

【技术实现步骤摘要】
一种三元乙丙橡胶泡沫材料及其制备方法和用途
本专利技术涉及一种泡沫材料，特别是涉及一种三元乙丙橡胶泡沫材料及其制备方法和用途。
技术介绍
随着环境和能源危机，汽车轻量化受到政府部门和汽车行业从业者的广泛关注。为了达到汽车轻量化效果，EPDM由于其低密度0.87g/cm3，耐腐蚀性等性能被广泛应用在汽车保险杠上。汽车保险杠是吸收和缓和外界冲击力、防护车身前后部的安全装置。对汽车或驾驶员在冲撞受力的时候，产生缓冲的作用。保险杠材料失效的现象比较复杂，但强度不足引起的失效现象主要还是屈服和断裂两种现象，对于保险杠系统通常以屈服形式失效。保险杠在设计时主要考虑车辆行驶冲撞时防止车辆损坏。在选用材料时，需要流动性好，耐热，耐化学药品性能好，表面硬度高，耐老化性能好，耐磨性能好。而如何在保证轻量化的基础上达到上述效果是急需解决的问题。
技术实现思路
鉴于以上所述现有技术的缺点，本专利技术的目的在于提供一种三元乙丙橡胶泡沫材料，用于解决现有技术中的问题。为实现上述目的及其他相关目的，本专利技术是通过以下技术方案获得的。本专利技术提供一种三元乙丙橡胶泡沫材料的制备方法，将造孔材料与三元乙丙橡胶基体复合，本文档来自技高网...

【技术保护点】
1.一种三元乙丙橡胶泡沫材料的制备方法，其特征在于，所述的制备方法包括以下步骤：将造孔材料与三元乙丙橡胶基体复合，采用HF溶液腐蚀剔除造孔材料即形成所述三元乙丙橡胶泡沫材料。

【技术特征摘要】
1.一种三元乙丙橡胶泡沫材料的制备方法，其特征在于，所述的制备方法包括以下步骤：将造孔材料与三元乙丙橡胶基体复合，采用HF溶液腐蚀剔除造孔材料即形成所述三元乙丙橡胶泡沫材料。2.根据权利要求1所述制备方法，其特征在于，所述复合的时机为在三元乙丙橡胶基体制备时或在三元乙丙橡胶基体制备完成后。3.根据权利要求1所述制备方法，其特征在于，所述造孔材料为具有三维多孔结构的Ti材料。4.根据权利要求3所述制备方法，其特征在于，所述Ti材料包括Ti丝，Ti纤维或者Ti管中的一种或多种。5.根据权利要...

【专利技术属性】
技术研发人员：江国锋，刘福强，张俊杰，
申请(专利权)人：上海赛科利汽车模具技术应用有限公司，
类型：发明
国别省市：上海,31