一种耐候聚烯烃母粒的制备方法技术

本发明专利技术涉及一种耐候聚烯烃母粒的制备方法，包括以下步骤：称取一定量的聚烯烃、纳米SiO2、柠檬酸钕、钛酸酯偶联剂、抗氧剂；将它们投入高速搅拌机混合，待混合均匀，放入双螺杆挤出机中挤出造粒，烘干既得耐候母粒。本申请合成了一种聚烯烃耐候母粒，它能很好地改善聚烯烃复合材料的耐候性能，这具有重要的意义，也具有很大的推广价值。

A Method for Preparing Weatherproof Polyolefin Masterbatch

The invention relates to a preparation method of weatherproof polyolefin masterbatch, which comprises the following steps: weighing a certain amount of polyolefin, nano-SiO 2, neodymium citrate, titanate coupling agent and antioxidant; mixing them in a high-speed mixer, waiting for uniform mixing, extruding and granulating in a twin-screw extruder, drying the obtained weatherproof masterbatch. In this application, a kind of polyolefin weatherproof masterbatch was synthesized, which can improve the weatherproof performance of polyolefin composites very well, which has important significance and great popularization value.

【技术实现步骤摘要】
一种耐候聚烯烃母粒的制备方法
本专利技术属于高分子材料
，特别是指一种耐候聚烯烃母粒的制备方法。
技术介绍
塑料暴露在日光或强的荧光下，会出现外观和物理机械性能劣化，通常表现为变色、失去光泽、出现银纹、侵蚀、龟裂以及物理性能下降等，这种现象称为光老化。鉴于此原因，本技术创新制得一种耐候聚烯烃母粒及其制备方法，改善现在聚烯烃塑料的耐候性能，这种耐候母粒至今尚未见于报道，这对于扩展耐候母粒的应用具有非常重要的现实意义。
技术实现思路
本专利技术的目的是提供一种耐候聚烯烃母粒的制备方法，以解决现有技术的耐候母粒的抗老化性能不能满足某些方面的要求的问题。本专利技术是通过以下技术方案实现的：一种耐候聚烯烃母粒的制备方法，包括以下步骤：(1)称取一定量的聚烯烃、纳米SiO2、柠檬酸钕、钛酸酯偶联剂、抗氧剂；(2)将它们投入高速搅拌机混合，待混合均匀，放入双螺杆挤出机中挤出造粒，烘干既得耐候母粒。步骤(1)中的聚烯烃、纳米SiO2、柠檬酸钕、钛酸酯偶联剂、抗氧剂的质量比为(100-120)：(10-16)：(1-3)：(0.1-0.3)：(0.2-0.4)。步骤(1)中的聚烯烃为PP、PE、PA本文档来自技高网...

【技术保护点】
1.一种耐候聚烯烃母粒的制备方法，其特征在于，包括以下步骤：(1)称取一定量的聚烯烃、纳米SiO2、柠檬酸钕、钛酸酯偶联剂、抗氧剂；(2)将它们投入高速搅拌机混合，待混合均匀，放入双螺杆挤出机中挤出造粒，烘干既得耐候母粒。

【技术特征摘要】
1.一种耐候聚烯烃母粒的制备方法，其特征在于，包括以下步骤：(1)称取一定量的聚烯烃、纳米SiO2、柠檬酸钕、钛酸酯偶联剂、抗氧剂；(2)将它们投入高速搅拌机混合，待混合均匀，放入双螺杆挤出机中挤出造粒，烘干既得耐候母粒。2.根据权利要求1所述的耐候聚烯烃母粒的制备方法，其特征在于，步骤(1)中的聚烯烃、纳米SiO2、柠檬酸钕、钛酸酯偶联剂、抗氧剂的质量比为(100-120)：(10-16)：(1-3)：(0.1-0.3)：(0.2-0.4)。3.根据权利要求1所述的耐候聚烯烃母粒的制备方法...

【专利技术属性】
技术研发人员：刘凯，王添琪，王泉杰，
申请(专利权)人：安徽江淮汽车集团股份有限公司，
类型：发明
国别省市：安徽,34