The invention discloses a preparation method of a shopping bag handheld bag carrier with better elasticity and comfort. The preparation method includes: weighing the mass fraction of styrene-butadiene rubber (SBR) and the mixture, in which 55.5 copies of the mixture are added when rubber is mixed; then, SBR is baked, cut, moulded and mixed separately; finally, the obtained mixture is put into the injection moulding machine from the left of the mould. Mixture was injected into the right two runners and cured for 8-10 minutes at 180 C under 5-8 MPa pressure. The elastic handheld bag carrier has the advantages of simple process, high production efficiency, good elasticity, good comfort, long service life and easy to carry. Cure into a comfortable shape. The elastic handheld bag carrier has the lowest tensile strength of 25.4 MPa and the highest wear resistance of 0.16 cm.
【技术实现步骤摘要】
一种弹性手握式拎袋器制备方法
本专利技术涉及购物袋拎袋器领域，涉及一种弹性手握式拎袋器的制备方法。
技术介绍
塑料袋是购物过程中使用最多的包装用品，是一种便携式生活用品，因其使用方便质轻价格低廉，可以使人们在购物时可以一次携带更多物品，广泛被人们使用。但当塑料袋中的物品较重时，长时间使用会造成勒手使得血液畅通困难。为了解决这一问题开始出现拎袋器，国内市场上的大多数拎袋器是由金属构成携带也不方便，这种拎袋器在使用时不易弯曲，容易刮破购物袋或者手，在用力掰弯后又不能容易的让它恢复使用之前的状态，购物袋一旦负荷重会勒手阻止血液流通。这种金属拎袋器使用一段时间以后容易产生铁锈，质量不好的甚至会出现掉下金属屑的情况。还有少数的拎袋器在金属的外边涂了一层带有颜色的油漆，而这种涂油漆的拎袋器在使用一段时间以后油漆也会发现脱落情况，长时间使用油漆会对皮肤造成伤害。最近一段时间出现了一种塑料拎袋器，这种拎袋器脆性大，弯曲性不好。另外，塑料拎袋器因其脆性大容易断裂，冬天更容易脆断，这可能会对手造成伤害，不是大多数人喜欢的选择。市场上公开出售一种硅胶提袋器，这种提袋器虽然解决了减少勒手...
【技术保护点】
1.一种弹性手握式拎袋器的制备方法，其特征在于，首先称量丁苯橡胶和配合剂质量分数；然后将丁苯橡胶分别进行烘胶、切胶、塑炼、混炼；最后将所得混炼胶放入注压成型机中固化成舒适形状。
【技术特征摘要】
1.一种弹性手握式拎袋器的制备方法，其特征在于，首先称量丁苯橡胶和配合剂质量分数；然后将丁苯橡胶分别进行烘胶、切胶、塑炼、混炼；最后将所得混炼胶放入注压成型机中固化成舒适形状。2.根据权利要求1所述的一种弹性手握式拎袋器的制备方法，其特征在于所述的丁苯橡胶和配合剂质量比为100：55.5。3.根据权利要求1所述的一种弹性手握式拎袋器的制备方法，其特征在于所述的塑炼工艺条件为35～45℃时间5分钟，塑炼工艺条件为45～50℃时间10分钟。4.根据权利要求1所述的一种弹性手握式拎袋器...
【专利技术属性】
技术研发人员：武卫莉，陈丰雨，李响，
申请(专利权)人：齐齐哈尔大学，
类型：发明
国别省市：黑龙江,23