The invention discloses a cemented carbide device and a preparation method thereof. The cemented carbide device of the invention comprises a cemented carbide matrix, and the surface of the cemented carbide matrix is successively bonded with a CoBx layer and a diamond film layer. The preparation method of the cemented carbide device includes thermal oxidation treatment of the cemented carbide matrix, acidification treatment of the cemented carbide matrix, boronization treatment of the cemented carbide matrix and growth of a diamond film on the surface of the cemented carbide matrix. The diamond film layer contained in the cemented carbide device of the invention has strong bonding force and prolongs the service life of the cemented carbide device.
【技术实现步骤摘要】
硬质合金器件及其制备方法
本专利技术属于超硬复合材料
，具体的是涉及一种硬质合金器件及其制备方法。
技术介绍
有色金属如铝合金、钛合金等具有高比强度，耐磨性、耐腐蚀性好，抗疲劳能力强，质量轻等优异的性能，是航空航天、汽车、轨道交通等领域的理想结构材料，但是其难加工特性严重阻碍了这类材料的规模化应用。如铝合金切削加工过程中出现的粘刀和积屑瘤现象严重，不仅影响后续碎屑的剥落，严重时会直接撕裂工件。钛合金由于高温化学活性高，导热性差，弹性模量低，与其他金属摩擦系数大等特性，造成切削温度高，单位面积切削力大，刀具磨损严重，刀具寿命低以及表面加工质量差等问题，普通刀具已经难以满足切削加工需求。其中，硬质合金刀具具有硬度高，韧性好等一系列的优点，被广泛应用于金属如有色金属的切割行业中，但是单一的硬质合金材料已经无法满足工业加工方面的需求，单一的硬质合金刀具切割有色金属，由于硬质合金刀具使用寿命有限，在使用过程中需要定期频繁更换，造成了硬质合金材料的浪费。因此全球刀具界都在尝试各种方法如：刀片基底、几何角度、涂层技术等来满足钛合金和铝合金的加工需求。在硬质合金刀具添加超硬...
【技术保护点】
1.一种硬质合金器件，包括硬质合金基体，在所述硬质合金基体表面依次结合有CoBx层和金刚石膜层；其中，x为1‑3。
【技术特征摘要】
1.一种硬质合金器件，包括硬质合金基体，在所述硬质合金基体表面依次结合有CoBx层和金刚石膜层；其中，x为1-3。2.根据权利要求1所述的硬质合金器件，其特征在于：所述CoBx层的厚度为1-3μm；和/或所述金刚石膜层的厚度为1-3mm。3.根据权利要求1所述的硬质合金器件，其特征在于：所述硬质合金基体是被依次经热氧化处理和酸化处理的硬质合金基体。4.根据权利要求3所述的硬质合金器件，其特征在于：所述热氧化处理的氧化温度为400-800℃，氧化时间为0.5-1h。5.根据权利要求1-4任一所述的硬质合金器件，其特征在于：所述硬质合金基体或所述硬质合金器件为模具、零部件、生物医疗器件、刀具、车削刀片中的任一种。6.一种硬质合金器件的制备方法，包括如下步骤：将硬质合金基体进行热氧化处理，在所述硬质合金基体表面生成一层氧化物层；将经热氧化处理的所述硬质合金基体进行酸化处理，除去所述氧化层；将经酸化处理的所述硬质合金基体进行...
【专利技术属性】
技术研发人员：唐永炳，谷继腾，杨扬，
申请(专利权)人：深圳先进技术研究院，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。