The invention discloses a preparation method of heat preservation material for greenhouse wall, which comprises the following steps: (1) taking straw ash and fly ash and passing through 120 mesh sieve after crushing; (2) putting 18 25 parts of straw ash, 18 25 parts of fly ash, 25 40 parts of cement, 30 40 parts of perlite, 15 22 parts of ceramics, 3 6 parts of hydrophobic agent, 3 6 parts of penetrant, 2 5 parts of curing agent and 2 5 parts of activator into mixer. Uniform; (3) add 85 100 portions of water to the mixture, mix it into slurry, then pour it into the mould to press and shape, and maintain it for 15 20 hours to get the finished product. The preparation method has the advantages of simple process, good thermal insulation effect, excellent strength and weatherability, long service life, environmental protection and non-toxicity.
【技术实现步骤摘要】
一种温室墙体保温材料的制备方法
本专利技术涉及保温材料
，具体涉及一种温室墙体保温材料的制备方法。
技术介绍
温室又称暖房，能透光、保温(或加温)，是用来栽培植物的设施。在不适宜植物生长的季节，能提供温室生育期和增加产量，多用于低温季节喜温蔬菜、花卉、林木等植物栽培或育苗等。温室的类型包括种植温室、养殖温室、展览温室、实验温室、餐饮温室、娱乐温室等；温室系统的设计包括增温系统、保温系统、降温系统、通风系统、控制系统、灌溉系统等；大棚只是简单的塑料薄膜和骨架结构，其内部设施很少，没有温室要求的高。因此严格说来，温室比大棚设备要求更高。对于温室而言，墙体保温是基本要求，现有的提高墙体保温性能的方法是在墙体的表面涂保温材料，但是现有的保温材料保温效果不好，并且强度低、耐候性差，在产品使用后期容易出现空鼓开裂等现象，不能满足使用需求。因此，墙体保温材料的综合性能需要进一步地提高。
技术实现思路
有鉴于此，本专利技术的目的在于提供一种保温隔热效果好、强度和耐候性优、使用寿命长的墙体保温材料制备方法。为实现上述目的，本专利技术采用的技术方案是：一种温室墙体保温材料的制备方法...
【技术保护点】
1.一种温室墙体保温材料的制备方法，其特征在于：包括以下步骤：(1)取秸秆灰、粉煤灰粉碎后过120目筛；(2)将秸秆灰18‑25份、粉煤灰18‑25份、水泥25‑40份、珍珠岩30‑40份、陶粒15‑22份、憎水剂3‑6份、渗透剂3‑6份、固化剂2‑5份、激发剂2‑5份放入搅拌机内混合均匀；(3)向混合物料中加水85‑100份，搅拌成浆料后倒入模具内压制成型，养护15‑20小时后得成品。
【技术特征摘要】
1.一种温室墙体保温材料的制备方法，其特征在于：包括以下步骤：(1)取秸秆灰、粉煤灰粉碎后过120目筛；(2)将秸秆灰18-25份、粉煤灰18-25份、水泥25-40份、珍珠岩30-40份、陶粒15-22份、憎水剂3-6份、渗透剂3-6份、固化剂2-5份、激发剂2-5份放入搅拌机内混合均匀；(3)向混合物料中加水85-100份，搅拌成浆料后倒入模具内压制成型，养护15-20小时后得成品。2.根据权利要求1所述的一种温室墙体保温材料的制备方法，其特征在于：所述憎水剂为有机硅。3.根据权利要求1所述的一种温室墙体...